鋼材再現溶接熱影響部の変態挙動におよぼす成分元素の影響(第 2 報) : 溶接用 SH-CCT 図におよぼす Si の影響

概要

論文の詳細を見る
The effect of Si on transformation behaviour in synthetic weld heat-affected zone of steel was investigated using simplified steels made of pure metals and graphite. Si element did not almost influence ferrite transformation region in SH-CCT diagram for welding, and displaced slightly pearlite transformation region to a longer time and to a higher reaction temperature. Zw (Zwischenstufengefuge) rmat transformationregion was present on the side of very short time regardless of Si content, and existed to longer time in case of higher Si content. Cz' which is critical cooling time to obtain from SH-CCT diagram for welding could not measure because Cz' was too small. Cf' was a little influenced by Si, and it was small. Cp' and Ce' increased with Si content. In the region of middle cooling time (cooling time from A_3 to 500℃; 6∿60sec), massive ferrite grew slightly large, and Zw precipitated easily with Si content. Morphology of Zw appeared that austenite between both ferrite sideplates or both rodlike ferrite decomposed to ferrite and relative large cementite. In the region of shorter cooling time (cooling time from A_3 to 500℃; under 6 sec), ferrite grew to long ferrite sideplate and long needlelike ferrite by Si content, and morphology of pearlite was influenced by Si, too. Degenerate pearlite formation was difficult with Si, and the volume of pearlite was decreased by Si content increased. The hardness of martensite was not so influenced by Si. The hardenability curves in synthetic weld affected zone of steels raised with Si content, but Si above 1.0% did not influenced to the hardenability curves. heat-Though Si diplaced slightly longer the cooling time which hardness was rapidly decrease, it seems that Si dose not strongly influence to hardenability of weld heat-affected zone of steels.
1975-02-05

鋼材再現溶接熱影響部の変態挙動におよぼす成分元素の影響(第 2 報) : 溶接用 SH-CCT 図におよぼす Si の影響

スポンサーリンク

概要

著者

関連論文

スポンサーリンク