405 ステンレスクラッド鋼の溶接割れの研究(第 1 報) : 溶接割れの再現とその防止法
スポンサーリンク
概要
- 論文の詳細を見る
AISI 405 stainless steel and its clad steel are widely used in chemical apparatus, such as oil refiners, heat exchangers and so on. Several cracks are often found in the weldment with the same chemical composition electrode (D410Nb) after welding or annealing. Investigations on phenomena of these cracking and their prevention were carried out. Conclusions are as follows. 1) Delayed cracking with very long incubation period occurs in 405 stainless steel weldment; this was never experienced in the structural steel weldment. 2) These cracks are prevented by preheating and adoption of MIG welding. Reducing the hydrogen content of deposited metal is most necessary to prevent these cracks. 3) Cracking occurs in high Cr content weldment such as 13Cr, 17Cr, and even in almost ferrite structure. These phenomena are very different from those in structural steel.
- 社団法人溶接学会の論文
- 1970-07-25
著者
関連論文
- 114 405ステンレスクラッド鋼の溶接に関する研究(第4報)
- 246 405ステンレスクラッド鋼の溶接に関する研究(第3報)
- 336 ステンレス鋼肉盛溶接部の剥離割れに関する研究(第2報)
- 113 ステンレス鋼肉盛溶接部の剥離割れに関する研究(第1報)
- 119 炭素鋼とオーステナイト鋼異材継手部の溶接割れについて
- 厚板溶接部の溶接割れ防止の研究(第二報)
- 厚板溶接部の溶接割れ防止の研究(第 1 報) : 溶接金属中の拡散性水素の分布と後熱処理によるその変化
- 246 厚板溶接部の溶接割れに関する研究(第2報)
- 104 厚板溶接部の溶接割れに関する研究(第1報)
- 鉄鋼溶着金属の異常破面に関する研究(第 2 報) : エレクトロスラッグ溶着金属と水素添加溶着金属の異常破面について
- 107 溶着金属中の拡散性水素量の測定に関する一考察
- 420 フェライト系ステンレス鋼の水素脆化について
- 17 Cr 不銹鋼の潜弧溶接について
- 405 ステンレス鋼溶接継手の曲げ延性改善の研究(第 2 報) : 化学組成の影響
- 405 ステンレス鋼溶接継手の曲げ延性改善の研究(第 1 報) : 後熱処理による改善
- 405 ステンレスクラッド鋼の溶接割れの研究(第 2 報) : 拡散性水素量の溶接割れにおよぼす影響
- 405 ステンレスクラッド鋼の溶接割れの研究(第 1 報) : 溶接割れの再現とその防止法
- 132 405ステンレス鋼溶接継手の延性に関する研究
- (91) オーステナイト系ステンレス鋼の潜弧溶接(昭和 37 年度秋季全国大会講演概要)
- (105) モネルメタルの肉盛溶接の研究(第 1 報)
- 48 板状電極式エレクトロスラグ溶接
- LMG 用 9% Ni 鋼のプラズマアーク溶接の研究
- (44) Ti-Fe爆発圧接界面の波状塑性変形について
- (13) 405ステンレスクラツド鋼の遲れ割れについて(2)
- (12) 405ステンレスクラツド鋼の遲れ割れについて(1)
- (11) 405ステンレス鋼溶接々手の曲げ性貭の改善の研究