HT60 高張力鋼の溶接用連続冷却変態図

概要

論文の詳細を見る
1) Continuous cooling transformation diagrams are constructed for six kinds of HT-60 strength steels, (four normalized steels, two heat-treated steels) by using the new apparatuses which can automatically reproduce any weld thermal cycle (maximum heating temperature 1350℃). 2) The critical cooling time C'_f derived from those CCT diagrams, i.e. the critical cooling time with regard to the first emergence of proeutictiod ferrite, is obtaind as follows, steel S6 : 1.8sec, S5 : 2.9sec, S1 : 3.2sec, S3 : 4.2sec, S2 : 0.8sec, S4 : 7.4sec. 3) It should be mentioned that the judgement of weldability with value of C'_f is in good accord with the result of other weldability tests, i.e. the hardness test with taper specimen, the bead bend ductility test, the maximum hardness test in H.A.Z. and the synthetic H.A.Z. ductility test, The value of C'_f is considered on important factor of weldability for ductility of weld heat affect zone and weld cracking susceptibility.
社団法人溶接学会の論文
1962-02-25