Porosity Caused by Hydrogen in Horizontal Fillet Welding
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate the behavior of porosity caused by hydrogen in horizontal fillet welding, the growth and the distribution of porosity, were studied using flux coated electrodes with various water contents. 1. Growth of porosity The growth of porosity becomes most remarkable when the hydrogen content of the weld is in a certain value, i.e. 15-17 cc/100 gr diffusible hydrogen content. At higher hydrogen content, the pores become smaller. 2. Distribution of porosity According to the measurements of length diameter of pore, pores in a weld may be classified into following types : A. Pores with length shorter than l_1 (≈1.2 mm) B. Pores with length longer than l_2 (l_2<l_1) And the pores with length l_1-l_2 are very few. These phenomena were investigated assuming a growth mechanism which was obtained by the relationship between tendency of porosity formation and behavior of molten metal.
- 社団法人溶接学会の論文
著者
-
Honma Hiroyuki
Products Res. & Dev. Lab. Nippon Steel Corp.
-
Mori Naomichi
Products Res. & Dev. Lab. Nippon Steel Corp.
-
TSUNETOMI Eiichi
Products Res. & Dev. Lab., Nippon Steel Corp.
-
ISHIZAKI Keizo
Japan Institute of Technology
-
Tsunetomi Eiichi
Products Res. & Dev. Lab. Nippon Steel Corp.