A Study of the Magnetoresistance Behavior of Co/Zr/Cu and Co/Ag/Cu Artificial Superlattices

スポンサーリンク

概要

• 論文の詳細を見る

• Ultrarhin (1〜3Å) zirconium and silver film was inserted into the interface of Co/Cu artificial superlattices, and the effect on the magnetoresistance was investigated. As zirconium layer was inserted, the magnetoresistance decreased drastically and the antiferromagnetic coupling did not occur. In case of silver insertion, there is no significant change at the as-deposit state. After heat treatment, however, the antiferromagnetic coupling and the magnetoresistance ratio of silver inserted Co/Cu artificial superlattices increased more than twice. The increase of GMR is caused by the promotion of the composition profile at the interface of cobalt, which was confirmed by the ^<59>Co ferromagnetic resonance (FMR) analysis.

• 社団法人電子情報通信学会の論文
• 1995-11-24

著者

• Park Joo-wook

  School Of Electrical Engineering Seoul National University

• Park Joo-wook

  Dept. Of Metallurgical Engineering Seoul National University

• Joo Seung-K

  Dept. of Metallurgical Engineering, Seoul National University

• Joo Seung-k

  Dept. Of Metallurgical Engineering Seoul National University

関連論文

• A Study of the Magnetoresistance Behavior of Co/Zr/Cu and Co/Ag/Cu Artificial Superlattices
• A Study of the Magnetoresistance Behavior of Co/Zr/Cu and Co/Ag/Cu Artificial Superlattices

スポンサーリンク