織物の一時加工剤としての水溶性ケラチンタンパクの利用 : 化学繊維の親水性および帯電性への影響
スポンサーリンク
概要
- 論文の詳細を見る
For the re-utilization of waste or used wool fibers, an attempt was made to apply the water-soluble keratin extracted from wool oxidized with performic acid to the additive finish of textile goods. With the amount of the keratin adsorbed on these fabrics, the moisture regains of polyester (PET), acrylic (ACR) and cellulose acetate (ACE) fabrics generally increased and the contact angles of water on the fabric surfaces decreased. As a result of the treatment, the surface resistivities of PET fabrics under 65 and 85% RH both decreased, while neither the resistivity of ACR under 65% RH nor that of ACE under 85% RH decreased. Further, the resistivities were almost unchanged, even after rubbing of the fabric surfac es with a pilling tester.
- 社団法人日本家政学会の論文
- 1998-01-15
著者
関連論文
- 羊毛の化学修飾とセット性--イソシアナ-トおよびグリシド-ル処理羊毛のセット性
- 羊毛の化学修飾とセット性--イソシアナ-ト処理羊毛のセット挙動
- ビスコ-スレ-ヨンのメタ過ヨウ素酸ナトリウム酸化の機械的性質におよぼす影響
- 天然染料染色布上の媒染剤量のICP-AES並びに蛍光X線による分析
- 織物の一時加工剤としての水溶性ケラチンタンパクの利用 : 化学繊維の親水性および帯電性への影響
- 可溶性ケラチンタンパクを用いた処理の織物の染色性に及ぼす影響
- 電子顕微鏡による伸長セット処理羊毛繊維の形態観察
- 3種の試験法により評価したブチルおよびフェニルイソシアナ-ト処理羊毛のセット性
- 化学処理による羊毛への消臭機能の付与
- 羊毛の吸湿挙動に及ぼすサクシニル化の影響
- 考古学と繊維材料学の接点
- 蝦夷錦の織物構造(I) (北方研究)
- 唐招提寺所蔵国宝「方円採糸花網」の復元的研究
- 廃棄羊毛繊維の再使用の提案 : 羊毛の化学修飾による高吸水性および吸湿性の付与
- 染色したセルロース繊維の光劣化について
- 天然染料を用いて媒染染色した麻布の光劣化?
- 東京とハノイの衣生活 : 女子学生の着装意識と衣服管理
- 天然繊維の劣化と保存環境
- 出土繊維鑑別のための基礎的研究-各種麻繊維の炭化による形態変化-
- 天然繊維製品の光劣化--染織文化財保存の観点から
- シアノエチル化アミロペクチンの誘電特性
- イソシアナートおよびエポキシド処理羊毛のセット性
- イソシアナート化合物による羊毛の処理とその機械的性質への影響
- エポキシド化合物を用いた羊毛の処理とその機械的性質への影響
- 羊毛の酸化およびサクシニル化による消臭機能の付与 : アンモニアおよびアルキルアミンに対する消臭性
- 昭和女子大学における女性の再就職支援