Development of Metal-resin Composite Restorative Material Part 5: Evaluation of the Bonding between Ag-Sn Particle and 4-META Coupling Agent of the Metal-resin Composite
スポンサーリンク
概要
- 論文の詳細を見る
This study evaluated the oxide characteristics on a Ag-Sn particle surface modified by acid and heat in order to understand the bonding mechanism. Nine different Ag-Sn particles including standard Sn, SnO and SnO_2 were evaluated by X-ray Photoelectron Spectroscopy (XPS). The particles were also used for preparing the composite to test the flexural properties following the ISO 4049. A high correlation between flexural strength of the composites and Sn3d binding energy of their filler particles was found. Different oxide forms (SnO and SnO_2) showed different adhesive abilities to bond with 4-META, regarding the difference in flexural strength of the composite. The highest flexural strength composite showed Sn3d binding energy of its filler at 486.4 eV, which was the SnO binding area. This implies that SnO was responsible for a good bond between particle surface and 4-META coupling agent.
- 日本歯科理工学会の論文
著者
-
Ogura H
Department Of Dental Materials Science School Of Life Dentistry At Niigata The Nippon Dental Univers
-
Ogura Hideo
Nippon Dental Univ. Niigata Jpn
-
Ogura Hideo
Department Of Dental Materials Science
-
Urapepon Somchai
Prosthodontics Department Faculty Of Dentistry Mahidol University
-
Urapepon Somchai
Department Of Dental Materials Science School Of Dentistry At Niigata The Nippon Dental Univ. Japan
-
Kakuta Kiyoshi
Department Of Dental Materials Science School Of Dentistry At Niigata The Nippon Dental University
-
Kakuta Kiyoshi
Nippon Dental Univ. Niigata Jpn
-
Ogura Hideo
Department Of Dental Materials Science School Of Dentistry At Niigata The Nippon Dental Univ. Japan
-
OGURA Hideo
Department of Dental Materials Science, School of Life Dentistry at Niigata, The Nippon Dental University
関連論文
- Setting and Flexural Properties of Metal-Resin Composite Using Ag-Cu Particles as Filler and Chemical Accelerator
- Polymerization of UDMA Using Zinc Particles and 4-META with and without BPO
- New Initiation System for Resin Polymerization using Metal Particles and 4-META
- Effects of Occlusal and Brushing Cycles on Wear of Composite Resins in Combined Wear Test
- Correlation between Accuracy of Crowns Fabricated Using CAD/CAM and Elastic Deformation of CAD/CAM Materials
- Infliximab Treatment for Refractory Kawasaki Disease With Coronary Artery Aneurysm : A 1-Month-Old Girl
- Wear Test Combining Simulated Occlusal Wear and Toothbrush Wear
- Machining Accuracy of CAD/CAM Ceramic Crowns Fabricated with Repeated Machining Using the Same Diamond Bur
- Durability of Tungsten Carbide Burs for the Fabrication of Titanium Crowns using Dental CAD/CAM
- Effect of additive metals, Sn, Ga, and In in Ag-Pd-Au-Cu alloys on initial bond strength of 4-META adhesive cement to these alloys