Hardness Measurement of Small Cementite Particles in 0.25 Carbon Steel Using an AFM Ultramicro Hardness Tester
スポンサーリンク
概要
- 論文の詳細を見る
The hardness of cementite spheroidized S25C steel was measured, using an AFM ultramicro hardness tester and a special lever that has a three-sided pyramidal diamond indenter with an apical angle of 60°. A clear AFM image of the specimen surface etched in a solution of 3% nitric acid and 97% alcohol enabled us to distinguish small cementite particles with a diameter of less than 1μm. Using AFM imaging, we obtained force-penetration curves for small cementite particles as well as the ferrite portion of S25C steel. The curves show yield behavior. Below the yield force where the penetration depth was less than 30nm, the experimental curve agrees well with the theoretical one. The normalized yield stress, τ_Y/G, is 0.46 for cementite particles and 0.24 for the ferrite portion. These values are nearly equal to those for glass and silicon, and for SNCM439 steel, respectively. It is concluded that the hardness measurement of the materials containing small particles was realized in the nanoscopic region, using the AFM ultramicro hardness tester with a special lever having a three-sided pyramidal diamond indenter with an apical angle of 60°.
- 一般社団法人日本機械学会の論文
- 1999-04-15
著者
-
MIYAHARA Kensuke
Materials Information Technology Station, National Institute for Materials Science
-
Miyahara K
National Institute For Materials Science Materials Information Technology Station Fatigue Group
-
Miyahara Kensuke
Materials Information Technology Station National Institute For Materials Science
-
NAGASHIMA Nobuo
National Institute for Materials Science, Materials Information Technology Station, Fatigue Group
-
NAGASHIMA Nobuo
Strength and Life Evaluation Research Station, Frontier Research Center for Structural Materials, Na
-
MIYAHARA Kensuke
Strength and Life Evaluation Research Station, Frontier Research Center for Structural Materials, Na
-
MATSUOKA Saburo
Strength and Life Evaluation Research Station, Frontier Research Center for Structural Materials, Na
-
Nagashima Nobuo
National Institute For Materials Science Materials Information Technology Station Fatigue Group
関連論文
- Contribution of Microstructural Factors to Hardness Change during Creep Exposure in Mod.9Cr-1Mo Steel
- Development of an Atomic Force Microscope Ultra-Microhardness Tester with a Silicon Tip for High-Resolution AFM Imaging
- Hardness Measurement of Small Cementite Particles in 0.25 Carbon Steel Using an AFM Ultramicro Hardness Tester
- Nanoindentation Measurement for a Tungsten(001)Single Crystal
- Nanoscopic Hardness Measurement by Atomic Force Microscope
- In-Situ 0bservation of Metal Surfaces in Aqueous Solutions with an Electrochemical STM