Fracture Behaviours of CFRP Laminates in Mode I Interlaminar Fracture Toughness Testing

スポンサーリンク

概要

• 論文の詳細を見る

• Fracture behaviours in mode I delamination tests of CFRP(T300/2500)were studied at cross-head velocity V=0.005〜200 mm/min. In low velocity region, serrations due to repeated unstable fracture appear on load P-displacement δ curve, and they become conspicuous as V becomes smaller. The crack resistance force R evaluated by using the peak values of the serrated P-δ relation becomes larger with the decrease of V;the rate dependence of R is negative. On the other hand, at velocities higher than the critical one(V_C), there is nothing but fluctuations on P-δ relations. Although the rate dependence of R is extremely small, it is a positive value. Relaxation tests were also performed for specimens deformed at lower and higher velocities than V_C;at high velocity, load P decreases with time, while at low velocity, the load remains constant during relaxation test. The rate dependence and fracture behaviours have been discussed by using a model which takes the crack tip blunting effect into account.

• 一般社団法人日本機械学会の論文
• 1998-04-15

著者

• Nojima Taketoshi

  Dept.of Aeronautics And Astronautics Kyoto University

• KUSAKA Takayuki

  Hyogo Prefectural Institute of Industrial Research

関連論文

• Fracture Behaviours of CFRP Laminates in Mode I Interlaminar Fracture Toughness Testing

スポンサーリンク