Corrosion Resistance and Corrosion Fatigue Strength of Carbon Steel Coated with Chromium Nitride by Multistage PVD Method

スポンサーリンク

概要

• 論文の詳細を見る

• Chromium nitride(CrN) exhibits good corrosion resistance in addition to excellent electrical and mechanical properties. A decrease in the number of defects such as pinholes or voids formed during deposition is required for improvement of corrosion resistance and corrosion fatigue strength of coated materials. A multistage physical vapor deposition(PVD) method was proposed in order to fabricate dense thin-coating films. In an electrochemical anodic polarization test in aerated 2%H_2SO_4 solution, 0.37 wt%C steel that was coated with CrN thin film using the multistage PVD method showed better corrosion resistance than a specimen coated by a conventional method. This is due to a decrease in the number of small defects in the coating film deposited using the multistage PVD method. Evaluation of the corrosion fatigue strength of multistage-coated steel was performed by means of a cantilever-type rotating-bending fatigue test in 3%NaCl solution. The corrosion fatigue strength of multistage-coated steel was improved compared with that of the uncoated steel;however, the increase in fatigue strength was less in the multistage-coated specimen than in the specimen coated by the conventional method, contrary to the experimental results obtained from the anodic polarization test. It was pointed out that corrosion fatigue strength is dependent on not only the number of defects but also the shape of large defects in the coating film.

• 一般社団法人日本機械学会の論文
• 1997-10-15

著者

• Shiozawa Kazuaki

  Department Of Mechanical And Intellectual Systems Engineering Toyama University

• Motobayashi Kou

  Graduate School Of Toyama University

• Sonobe Masaru

  Graduate School Of Toyama University

関連論文

• Effect of Flaws in Coating Film on Fatigue Strength of Steel Coated with Titanium Nitride
• Crack Propagation behavior under Low-Cycle Corrosion Fatigue of A7003-T6 Aluminum Alloy
• Subsurface Crack Initiation and Propagation Mechanism under the Super-Long Fatigue Regime for High Speed Tool Steel (JIS SKH51) by Fracture Surface Topographic Analysis (JSME Medal for Outstanding Paper in 2004)
• Effect of Microstructure on Creep and Creep-Fatigue behavior in Ti-6Al-4V Alloy at Elevated Temperature
• Corrosion Resistance and Corrosion Fatigue Strength of Carbon Steel Coated with Chromium Nitride by Multistage PVD Method

スポンサーリンク