High-Temperature Fatigue Crack Propagation Property of Mod.9Cr-1Mo Steel under Vacuum and Air Conditions

スポンサーリンク

概要

• 論文の詳細を見る

• Microcrack propagation behavior of Mod.9Cr-1Mo steel under high-temperature fatigue in vacuum and air conditions were periodically observed. Microcracks propagated in the direction normal to stress axis in vacuum while the microcracks propagated in the maximum shear direction in air condition. It was found that propagation rate in air was faster than that in vacuum until the crack grew 1 mm length due to oxidation effect which was insignificant for the crack larger than 1 mm. Acceleration of the crack propagation rate in the compression hold test was supposed to be caused by accumulation of tensile strain in the center of the specimen due to off-balance of strain distribution between tension and compression side.

• 一般社団法人日本機械学会の論文
• 1997-07-15

著者

• Ogata Takashi

  Central Research Institute Of Electric Power Industry

• Yamamoto Masato

  Central Research Institute Of Electric Power Industry

関連論文

• OS6-04 Development of Signal Processing Method for Fiber Optic AE Sensor Using Wavelet Analysis
• High-Temperature Fatigue Crack Propagation Property of Mod.9Cr-1Mo Steel under Vacuum and Air Conditions
• SA-02-3(094) Remaining Life Assessment Methods for Boiler Weldment Parts(Life Assessment of Thermal Power Plant 2)

スポンサーリンク