Magneto-optical investigation of near-surface micro-magnetic structure of FeNbCuSiB alloys
スポンサーリンク
概要
- 論文の詳細を見る
The results on the investigation of near-surface micro-magnetic structure of the as-cast and annealed at 550℃ for 1hr FeCuNbSiB ribbons are presented. The measurements were performed by using of the magneto-optical micro-magnetometer having the spatial resolution up to 〜0.3μm. The as-cast samples were amorphous and the annealed samples had nanocrystalline structure with typical grain sizes of 10 - 12 nm. The dispersion of magnetic anisotropy was discovered in the studied samples. As result, their local magnetic properties were inhomogeneous. The linear size of the magnetic inhomogeneities in the as-cast and annealed samples was equal to 〜 120 - 150 and 〜 50 - 70 μm, respectively. It was established that in the annealed samples the local initial magnetic permeability increases and the coercivity decreases (up to 10 times) with respect to those of the as-cast samples.
- 社団法人日本磁気学会の論文
- 1999-01-20
著者
-
Tsidaeva N
Pysical Faculty Of Moscow State University
-
Shalyguina E
Pysical Faculty Of Moscow State University
-
Shalyguina E.
Pysical Faculty of Moscow State University
-
Tsidaeva N.
Pysical Faculty of Moscow State University
-
Bekoeva L.
Pysical Faculty of Moscow State University
-
Tsidaeva N.I.
Pysical Faculty of Moscow State University
-
Shalyguina E.E.
Pysical Faculty of Moscow State University
-
Bekoeva L.M.
Pysical Faculty of Moscow State University