急冷凝固法で作製したCo-Zr-B合金のハード磁気特性(ハード磁性材料)
スポンサーリンク
概要
- 論文の詳細を見る
Microstructural studies revealed that a Co-Zr-B alloy ingot had coarse grains of Co_<23>Zr_6, Co_5Zr, and Co_3ZrB_2 phases. Melt-spinning of the alloy ingot resulted in the formation of fine equiaxed grains. The resultant melt-spun ribbons consisted of the Co_5Zr and Co_<23>Zr_6 phases and showed coercivities over 1 kOe. Heat treatment of Co-Zr-B melt-spun ribbons resulted in an increase in coercivity. The coercivity of annealed Co-Zr-B melt-spun ribbons was strongly dependent on the alloy composition. A high coercivity of 5 kOe was achieved in a composition of Co_<78>Zr_<18>B_4 and Co_<80>Zr_<18>B_2. The Co-Zr-B melt-spun ribbons exhibited a maximum energy product comparable to that of the hard ferrites.
- 社団法人日本磁気学会の論文
- 2004-03-01
著者
関連論文
- Sm-Fe系合金急冷薄帯の構造と磁気特性
- Pr-Fe-B系ナノコンポジット磁石の磁気特性
- 高性能希土類永久磁石の開発
- 磁界中放電プラズマ焼結法による希土類化合物の形態制御
- 新しいSm-Fe系金属間化合物の研究
- 冷間圧縮せん断法によるSm_2Fe_窒化化合物バルク磁石の作製
- Sm-Fe-N合金粉末の固化成形
- Co-Zr合金の磁気特性に対する添加元素の影響
- メカニカルアロイング法により作製したMn-Al-C合金粉末の磁気特性
- Nd-Fe-B系バルクナノコンポジット磁石の磁気特性
- 急冷凝固法で作製したCo-Zr-B合金のハード磁気特性(ハード磁性材料)
- 急冷凝固法で作製したCo-Zr-B合金のハード磁気特性
- 新しいハード磁性材料の開発
- 化学還元法で作製したCo系合金粉末のハード磁気特性
- メカニカルアロイング法により作製したTi-Fe合金の構造と水素吸蔵特性
- バルクナノコンポジット磁石の作製
- メカニカルアロイング法で作製したNd-Fe-B合金の磁気特性
- 急冷凝固法で作製したNb-Fe-B合金のメカニカルグライディング
- メカニカルアロイングによるNd-Fe-B合金の作製
- 低希土類組成Nd-Fe-Bアモルファス合金粉末の衝撃成形
- Sm-Fe-N系異方性磁石の磁気特性
- Sm_5Fe_系金属間化合物の磁気特性
- La-Co合金の磁気特性
- Sm-Fe系合金のハード磁気特性
- 冷間圧縮せん断法により作製したSm-Fe-N磁石の磁気特性
- 高保磁力Sm_5Fe_合金の磁気特性
- 希土類を含むガラススラグからの希土類の回収と分離
- 希土類磁石のガラススラグ法による分離・回収
- 高保磁力を有するサマリウム鉄系希土類磁石の磁気特性評価
- 冷間圧縮せん断法による希土類磁石の作製
- Nd-Fe-B合金の電気抵抗測定
- Sm_5Fe_系磁石の研究開発
- 急冷凝固法により作製したSm-Fe合金の磁気特性
- 新しい永久磁石材料の研究開発