Three types of LiNbO_3 single crystals were grown from melt doped with 1, 3 and 5 mol% of MgO. Homogeneities of these crystals without subgrain boundaries are useful enough for optical device substrates. No optical damage was observed in these crystals under irradiation of Ar laser with an incident power of 44 W/cm^2 and an exposure time of up to 10 min. However, optical damage was observed in the second harmonic generation of intracavity frequency doubling at room temperature with a diode-laser-pumped CW Nd: YAG laser and 1 mol% MgO doped LiNbO_3. On the other hand, the bulk laser damage threshold for MgO 1 mol% doped crystal is as high as 14 GW/cm^2 for pulse YLF laser (1.053,μm, 1 ns).
- 日本結晶成長学会の論文
- 1991-02-15
著者
関連論文
- マルチモードによる青色低ノイズ内部共振器型LD励起Cr:LiSrAlF_6-SHGレーザー
- 単ーモードによる低ノイズ青色発生LD励起Cr:LiSAF-SHGレーザ
- 高粘性融液からの高品位LiB_3O_5単結晶の育成 : 融液成長(一般)III
- LBO結晶とその全固体型青色SHGレーザーへの応用
- LD励起Cr : LiSAFレーザによる青色SHG
- フォトリフラクティブ用途LiTaO_3単結晶の開発
- 非コングルエント組成LiNbO_3単結晶とLiTaO_3単結晶の耐光損傷特性(LN,LT結晶の育成と光損傷)
- FZ法育成YIG結晶の鉄価数制御 : バルク成長シンポジュウムII
- 非コングルエント組成LiNbO_3単結晶の育成と評価 : 融液成長I
- MgO添加LiNbO_3単結晶の育成と光損傷特性(バルク成長)
- C-3 SAW素子用LiTaO_3基板材の音速変動要因(弾性表面波)