K-0811 炭素鋼配管の軽水炉環境中疲労き裂進展特性評価(S11-3 構造健全性評価(3))(S11 構造健全性評価)
スポンサーリンク
概要
- 論文の詳細を見る
To clarify the integrity of the piping of the highly aged light water reactor power plants, fatigue crack growth test was performed in air and in simulated BWR water environment using the pipe specimen (JIS STS410, 12inch) with inner surface cracks. Semi-elliptical cracks were made in inner surface of the base metal and welded region. The method for calculating stress intensity factor of surface crack on pipe was verified with the test in air. It was clarified that the crack growth rate in BWR water environment can apply to evaluate the crack growth of BWR plant piping. The present research was carried out by JAPEIC as one of research works entrusted by the Ministry of Economy, Trade and Industry (METI).
- 社団法人日本機械学会の論文
- 2001-08-22
著者
関連論文
- 754 軽水炉環境中における炭素鋼及び低合金鋼の疲労寿命評価
- 753 軽水炉環境中におけるオーステナイト系ステンレス鋼の疲労寿命評価
- 引張残留応力場から圧縮残留応力場にき裂が伝播する場合の溶接残留応力の再配分とき裂進展挙動
- 2937 発電用原子力設備に関する環境疲労評価ガイドラインについて
- 3214 簡易弾塑性解析における応力割り増し係数の開発
- F-1708 BWR環境中における炭素鋼の疲労き裂進展速度参照曲線の提案(S59-3 規格基準の高度化に関連する研究・開発状況(3))(S59 規格基準の高度化に関連する研究・開発状況)
- K-0811 炭素鋼配管の軽水炉環境中疲労き裂進展特性評価(S11-3 構造健全性評価(3))(S11 構造健全性評価)
- 608 軽水炉模擬環境中における炭素鋼の疲労き裂進展速度に及ぼす Rise time の影響
- 606 微小き裂を有する原子力プラント炭素鋼配管の健全性
- 602 低上部棚靭性を有する圧力容器の延性き裂成長挙動
- 引張残留応力場から圧縮残留応力場にき裂が伝播する場合の溶接残留応力の再配分とき裂進展挙動(OS6-3 損傷評価・計測,OS6 エネルギー機器の維持管理と健全性評価)
- 軽水炉長寿命化と材料技術 (特集 原子力発電の高経年化対策--軽水炉の長寿命化への取組み)