1122 パックアルミナイジングによる Fe-Al 金属間化合物被膜のすべり摩耗挙動

スポンサーリンク

概要

• 論文の詳細を見る

• FeAl and Fe_2Al_5 intermetallic compound coatings were formed on the low-carbon steel by pack aluminizing, and dry reciprocating sliding tests were carried out against a ball of SUJ2. It turned out that the wear loss of FeAl coating was smaller than that Fe_2Al_5 coating, and also that coefficient of friction of FeAl coating and that of Fe_2Al_5 coating after running of 500m are about 0.70 and 0.60,respectively. Wear behavior in the early stage was significantly different between FeAl and Fe_2Al_5 coatings. A Plastic deformation occurred on the wear side of FeAl coating, which appears to be adhesive wear, On the other hand, a large amount of cracks occurred in Fe_2Al_5 coating from early stage, which gave rise to a flaking.

• 2003-08-05

著者

• 新野邊 幸市

  松江高専

• 渡部 正氣

  松江高専

• 稲田 将人

  松江高専・専攻科

関連論文

• 熱処理によるチタンアルミ合金の結晶粒微細等軸化
• 605 繰返し摩擦によるアルミ拡散処理鋼に生じる構造(機械材料・新素材II,オーガナイズドセッション,人体のコンピュータモデルの作成とその応用,特別講演)
• 904 アルミ拡散処理をした鋼の繰返し摩擦による構造変化(機械材料・新素材)
• 1122 パックアルミナイジングによる Fe-Al 金属間化合物被膜のすべり摩耗挙動
• 拡散処理によるオーステナイトステンレス鋼への耐摩耗被膜の形成(J17-1 表面改質とトライボロジー(I),J17 表面改質とトライボロジー)
• 3138 ギヤホーニングに関する研究 : ツールマーク(S34-4 伝動装置の基礎と応用(4) 歯車の形状解析,ラック&ピニオン,その他,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
• チタンアルミ合金における過冷却生成したα_2相の分解挙動

スポンサーリンク