626 オーステナイト系ステンレス鋼溶接部の高温強度データと損傷事例
スポンサーリンク
概要
- 論文の詳細を見る
Many cracks occurred at 308 austenitic stainless welds made by flux cored arc welding(FCAW) process in hot-wall type fluid catalytic cracking(FCC) units operated at a service temperature of more than 640℃ in oil refineries. During investigation the cause of cracking, it was cleared that the high temperature characteristics of these welds such as creep strength at over 640℃ are not fully understood due to little available data. Among many factors that may have caused cracks, a small amount of Bi contained in the weld metals was considered to be the most predominant factor that deteriorated creep ductility and increased reheat cracking susceptibility of the weld metals. This report shows also the results of the effect of welding process and weld metal type on creep rupture properties that contain Bi free and Bi free weld metal.
- 一般社団法人日本機械学会の論文
- 2002-09-20
著者
関連論文
- 化学プラント設備の防食と肉盛溶接(溶接における腐食と防食)
- 溶接補修技術データベース(第IV部 企業における溶接・接合の情報デジタル化とその活用,溶接・接合における情報デジタル化の潮流)
- 347 裏波溶接用TIG溶加材の開発
- 219 347糸溶接金属の再熱割れ性について(第2報)
- 417 347系溶接金属の時効および水素脆化特性について
- 416 347系溶接金属の再熱割れ性について(第1報)
- 215 建築用高強度308Mo系フラックス入りワイヤの提案(第2報)(溶接冶金(II),平成19年度秋季全国大会)
- 法規・規格から見た石油・石油化学プラントの溶接補修--供用中圧力容器の肉盛り溶接補修に対する我国の各規格から見た概要
- 260 SUS836L溶接継手性能の調査
- 活性フラックスTIG溶接法の原理と実際 : 活性フラックスTIG溶接の実際
- 活性フラックス利用による深溶込み溶接
- 銅および銅合金の溶接(エンジニアリングデータシート)
- 214 建築用高強度308Mo系フラックス入りワイヤの提案(第1報)(溶接冶金(II),平成19年度秋季全国大会)
- 626 オーステナイト系ステンレス鋼溶接部の高温強度データと損傷事例
- 恒温保持過程における溶接金属の組織変化 : ステンレス鋼FCAW溶接金属における再然割れに関する研究(第5報)
- 維持規格適用上の課題
- 腐食から見た維持規格適用上の留意点
- 維持規格と腐食
- 他学・協会活動と維持規格
- 炭素鋼・ステンレス鋼の腐食対策 : 溶接部の腐食メカニズムと対策について
- 溶接材料開発