128 Fretting Fatigue Behavior in the Ultra High Cycle Regime
スポンサーリンク
概要
- 論文の詳細を見る
Research on fatigue behavior in the ultra high cycle regime has been recently focused since the fatigue mechanism and S-N behavior different from those observed less than (10)^7 cycles have been observed. It is also of importance from the viewpoint of the long-term service use of structures and machines. Limited research works have been available on fretting fatigue in the ultra high cycle regime, while lots of studies have been done on plain fatigue even in this regime. In the present study, a new machine for ultra high cycle fatigue test has been developed with an electro-magnetic vibrator. It was confirmed that fretting fatigue strength, lives, frictional force and relative slip amplitude were not significantly influenced by the cyclic loading rate up to 300 Hz, which was the present test condition for ultra high cycle fretting fatigue. The fretting fatigue strengths defined at (10)^7 cycles were effective up to (10)^8 and (10)^9 cycles for titanium alloy and aluminum alloy. The fretting fatigue crack initiated at the end region of fretting contact area even in the ultra high cycle regime, which indicated that the fatigue mechanism would not change even in the ultra high cycle regime. This might result from the singular stress field near the contact edge in fretting fatigue.
- 一般社団法人日本機械学会の論文
著者
-
SHIRAI S.
Department of Ophthalmology, Nagoya City University Medical. School
-
Mutoh Y.
Department Of Mechanical Engineering Nagaoka University Of Technology
-
Makabe J.
Department of Mechanical Engineering, Nagaoka University of Technology
-
Makabe J.
Department Of Mechanical Engineering Nagaoka University Of Technology
関連論文
- Developmental abnormalities of the optic nerve induced in mice by ochratoxin A : ABSTRACTS OF PAPERS PRESENTED at the TWENTY-SEVENTH ANNUAL MEETING of the JAPANESE TERATOLOGY SOCIETY TOKYO, JAPAN, JULY 17-18, 1987
- C-10 Histopathological Studies on Ocular Anomalies Associated with 13 Trisomy Syndrome.
- 128 Fretting Fatigue Behavior in the Ultra High Cycle Regime
- Effects of ethanol on the eye development in mouse fetuses : Abstracts of Papers Presented at the Thirty-Second Annual Meeting of the Japanese Teratology Society Tokyo, Japan, July 8-10, 1992
- 234 Effect of Microstructure on Fatigue Crack Growth Behavior of Structural steel