407 Solid State Lubricant Film Dispersed Nano-Cluster Diamond Powder

スポンサーリンク

概要

• 論文の詳細を見る

• For space mechanical components, the characteristics of silver thin film dispersed nano-cluster diamond powder as a solid lubricant film had been investigated. The silver films dispersed the cluster diamond powder were made on the 440C stainless steel disks under vacuum of 3×(10)^<-2>Pa at 1080K without graphitization of the nano-cluster diamond powder. Frictional characteristics of the films were investigated by a pin-on-disk friction test in injected nitrogen gas atmosphere (30%RH, 15% oxygen gas) and under ultra high vacuum of 2×(10)^<-6>Pa. Initial Hertzian contact pressure was set almost 0.7GPa. The sliding speed between the pin and the disk was about 30mm/s. Compared with ion-plated silver film, the lifetime of the film dispersed the nano-cluster diamond powder was 100 times longer in nitrogen gas atmosphere. The initial friction coefficient showed 0.2,and then it showed stable 0.4 for a while. The cluster diamond powder is considered to prevent the wear of the silver film.

• 一般社団法人日本機械学会の論文

著者

• Suzumura Akio

  Graduate School Of Science And Engineering Tokyo Institute Of Technology

• Yamazaki Takahisa

  Technology Research Department, National Space Development Agency of Japan (NASDA) Tsukuba Space Cen

• Yamazaki Takahisa

  Technology Research Department National Space Development Agency Of Japan (nasda) Tsukuba Space Cent

関連論文

• Braze Pressure Welding (BPW) : A New Method for High Quality Pressure Welding
• 414 Braze Pressure Welding (B. P. W.)-A New Method for High Quality Pressure Welding
• 407 Solid State Lubricant Film Dispersed Nano-Cluster Diamond Powder
• Effect of a Nickel-Iron Mixture of Weld Metal on Hydrogen Permeability at Various Temperatures in 316L Stainless Steel

スポンサーリンク