136 Tribological properties of a-C/a-C : Cr multilayer coatings

スポンサーリンク

概要

• 論文の詳細を見る

• Alternated a-C/a-C : Cr (about 2.5μm thickness) coatings were made by DC magnetron sputtering from graphite and Cr target in an argon discharge. Mechanical and tribological properties were measured by indentation, scratch and pin-on-disc test. The critical scratch load of a-C/a-C : Cr multilayer coatings for total failure is approach 100N. The friction coefficient remains within the range of 0.08-0.1 at loads between 10 and 40N during a pin-on-disc wear test. The wear depth only reaches 0.6μm after a one hour wear test. The surface of a-C/a-C : Cr multilayer coatings undergoes cyclic deformation, and failure eventually occurs as a result of fatigue. The greater compliance and fracture toughness of the a-C/a-C : Cr multilayer coatings allows greater strains or strain energy to be stored before coating failure, and hence significantly improves wear resistance

• 一般社団法人日本機械学会の論文

著者

• Lin H.

  Dept. Obst. And Gynec. Med. College. Natl. Taiwan Univ.

• Ma K.

  Dept. Of Mechanical Engineering Chung-hua University

• Lin H.

  Dept. Of Applied Physics National Defense University

• Chao C.

  Dept. Of Mechanical And Electro-mechanical Engineering Tam-kang University

• Chien H.

  Dept. Of Mechanical Engineering Chung-hua University

関連論文

• IS-16 Can a preoperative CA 125 Level Be a Criterion for Full Pelvic Lymphadenectomy in Surgical Staging of Endometrial Cancer?
• 139 Fabrication of Polymer Photonic Crystal Fiber
• 136 Tribological properties of a-C/a-C : Cr multilayer coatings
• 533 The influence of pregnancy and delivery on HBV amount of HBeAg-positive carrier mothers.
• 534 Anodic polarization study of nitinol thin films for electrochemical micromachining vascular stents

スポンサーリンク