920 SUS316鋼溶接継手の熱疲労挙動とδ-フェライト量の変化(GS-3 熱変形・高温疲労・熱疲労)
スポンサーリンク
概要
- 論文の詳細を見る
Thermomechanical fatigue (TMF) with temperature range 300-700℃ and isothermal fatigue behavior at 700℃ in air were studied on SUS 316 base metal and weld metal. TMF lives in base metal were a little shorter than isothermal fatigue lives. This is due to that the fracture mode in both loading was similar- a mixed type. On the other hand, a drastic reduction in life was noticed in weld metal under TMF in comparison with isothermal fatigue. This was attributed to the additional damage due to many independent subsurface cracks at σ phase boundaries and linkage of these cracks with the surface crack leading to rapid crack propagation. δ-ferrite in weld metal rapidly transformed to σ phase in both isothermal fatigue and TMF tests.
- 2000-03-16
著者
関連論文
- 710 ホイスト用リンクチェーンの疲労強度評価
- 3107 テルハのリンクチェーン破断事故解析(OS.10 故障診断・予知・メンテナンス・安全性)
- 新しい電磁式ワイヤロープ断線損傷検出法の開発
- 1522 フレッティング疲労強度に及ぼす試験装置およびパッドスパンの影響
- 2841 赤外線応力画像システムを用いた溶接継手の疲労き裂検出(S37-4 非破壊評価とモニタリング(4),S37 非破壊評価とモニタリング)
- 1404 つり荷走行中のラフテレンクレーンにおける応力頻度の計測
- 1403 ラフテレーンクレーン動作時のブーム応力について
- 920 SUS316鋼溶接継手の熱疲労挙動とδ-フェライト量の変化(GS-3 熱変形・高温疲労・熱疲労)
- 1402 作業場におけるラフテレーンクレーンの稼動時負荷測定
- 3024 ラフテレーンクレーンブーム部の動作別負荷測定
- 3023 ラチスジブ移動式クレーンの実働負荷について
- 1303 つり荷走行中のクローラクレーンにおける応力頻度の計測
- 1302 建設現場におけるタワー式クローラクレーンの作業時負荷について
- 418 ラチス式ジブクレーンの稼動時負荷について
- 440 Analysis of Ultrasonic Reflection by Wavelet Transform for Thermally Degraded Cr-Mo Steel
- 709 最近の材料損傷に起因する労働災害事例
- 454 赤外線計測による応力拡大係数範囲の測定精度改善に関する研究 : 第二報 数値解析を援用した精度改善(GS-12 き裂(3))