OS12(4)-18(OS12W0367) High Cycle Thermal Fatigue Crack Initiation and Growth Behavior in Simulated BWR Water Environment

スポンサーリンク

概要

• 論文の詳細を見る
• 一般社団法人日本機械学会の論文
• 2003-09-09

著者

• Miyazaki Katsumasa

  Mechanical Engineering Research Laboratory Hitachi Ltd.

• Hayashi Makoto

  Nuclear Systems Division Hitachi Ltd.

• Tanie Hisashi

  Mechanical Engineering Research Laboratory, Hitachi, Ltd.

• Tanie Hisashi

  Mechanical Engineering Research Laboratory Hitachi Ltd.

関連論文

• ICONE11-36546 DEVELOPMENT OF DUAL-PURPOSE METAL CASK FOR INTERIM STORAGE OF SPENT NUCLEAR FUEL (3) : A NEW TYPE OF DURABLE NEUTRON SHIELDING RESIN
• ICONE11-36551 DEVELOPMENT OF DUAL-PURPOSE METAL CASK FOR INTERIM STORAGE OF SPENT NUCLEAR FUEL (1) : OUTLINE OF CASK STRUCTURE
• ICONE11-36547 DEVELOPMENT OF DUAL-PURPOSE METAL CASK FOR INTERIM STORAGE OF SPENT NUCLEAR FUEL (2) : Evaluation of Structural Integrity of Dual-purpose Cask at 9 Meter Drop Test
• Analysis of Stress Intensity Factor due to Surface Crack Propagation in Residual Stress Fields Caused by Welding : Comparison of Influence Function Method and Inherent Strain Analysis(Fracture Mechanics)
• OS12(5)-23(OS12W0366) Initiation and Growth of Corrosion Pits and Its Effect on Corrosion Fatigue Strength in 13Cr Stainless Steel
• Fatigue Crack Propagation Analysis for Micro Solder Joints with Void
• OS12(5)-21(OS12W0406) Simplified Method to Calculate Stress Intensity Factors for a Surface Crack in a Weld of a Pipe Penetrating a Thick Plate with a Stub Tube
• OS12(4)-18(OS12W0367) High Cycle Thermal Fatigue Crack Initiation and Growth Behavior in Simulated BWR Water Environment

スポンサーリンク