FC 25 鋳鉄の衝撃による表面残留応力除去の挙動
スポンサーリンク
概要
- 論文の詳細を見る
The relief of surface residual stress in an FC25 pearlitic graphite cast iron plate has been experimentally studied under impact loading. Surface residual stress is relieved by impact repeated more than one hundred times. When the impact loading stress wave amplitude added to the residual stress is more than 0.025% offset stress in the materials, more residual stress is relieved. When the value is smaller than the added value, residual stress is not relieved. After the relief of surface residual stress under impact loading, the fatigue limit on the FC25 pearlitic graphite cast iron cannot be improved more than before, and remarkable change in residual stress was not observed after exposure in open air for one month.
- 一般社団法人日本機械学会の論文
- 1985-02-25
著者
関連論文
- 809 チタニウム線材の引抜き加工による残留応力と集合組織の X 線解析
- 705 炭素鋼線材の引抜き加工における残留応力と集合組織のX線解析について(GS-4・20 機械材料・材料加工(2))
- 1013 鋼線材の引抜き加工手法による残留応力と集合組織の研究(GS-4 材料加工)
- Al合金磁気ディスク基板のダイヤモンド切削による残留応力と変形
- 超精密加工面に関する研究(第3報) -表面残留応力と超精密切削の力学挙動の関係-
- 704 被覆膜生成による残留応力の挙動(GS-4 機械材料・材料加工(1))
- 319 伸線加工における欠陥発生の分子動力学モデルに関する検討(OS-3 転位・欠陥)
- 713 ダイス伸線における引抜き角の影響についての三次元弾塑性FEM解析(GS-4 機械材料・材料加工(3))
- 線材引抜き加工ダイの最適形状
- 712 管引抜き加工の各手法に対するコンピュータ・シミュレーション(GS-4 機械材料・材料加工(3))
- 710 超音波付加バテッドチューブ引抜き加工の研究(GS-4 機械材料・材料加工(3))
- 112 弾塑性FEM解析による伸線へのダイス形状の影響について(OS-4 機械加工)
- 1104 伸線ダイス形状による内部応力と残留応力分布に関する研究(GS-3 塑性加工)
- 1103 ダイス伸線における引抜き角度の三次元弾塑性FEM解析(GS-3 塑性加工)
- 1101 バテッドチューブ加工の研究(GS-3 塑性加工)
- 1012 超音波引抜き加工における潤滑剤の影響(GS-4 材料加工)
- Cu-Zn-Al形状記憶合金の結晶粒微細化による機械的性質および形状記憶熱エンジンの性能に及ぼす結晶粒径の影響
- 引抜き
- ダイス伸線におけるシェブロン・クラックと最適伸線条件へのダイス-ワイヤ接触長さ比の影響
- 超音波付加引張り変形をした銅--亜鉛合金のX線による格子欠陥解析
- β相形状記憶合金の変形状態と応力集中におよぼす弾性異方性の影響
- 弾性異方性の有限要素法による応力解析--銅系形状記憶合金に関する研究
- FC25鋳鉄の振動による表面残留応力除去と格子欠陥密度の挙動
- 残留応力の振動による除去の挙動
- FC 25 鋳鉄の衝撃による表面残留応力除去の挙動
- 機械材料の制振特性に関する研究
- FC25鋳鉄の振動による表面残留応力除去の挙動
- 残留応力の振動と衝動による緩和
- 1027 ナノ力学による伸線加工時の欠陥挙動と応力状態に関する検討(OS10.電子・原子・マルチシミュレーションに基づく材料特性評価(6:ナノクラスター・ナノチューブ),オーガナイズドセッション)