低サイクル疲労をうける切欠材でのき裂進展挙動
スポンサーリンク
概要
- 論文の詳細を見る
Smooth specimens and two types of notched specimens were made of high tensile strength steel (HT 60) and were low-cycle fatigued. In the tests, the growth of small surface cracks was monitored by means of replicas. The crack growth rate dl/dN was examined by the strain intensity factor range ΔK_ε. Firstly, the ΔK_ε of notched specimens was calculated from the nominal strain amplitude at notch roots. The dl/dN-ΔK_ε= relation in each type of specimen was approximately expressed by a linear line on a log-log diagram. However, the lines were different from that of smooth specimens, and depended upon the shapes of notches. Secondarily, the maximum strain amplitude at notch roots was obtained by the simple method. The ΔK_ε of notched specimens was calculated from it. The dl/ dN-ΔK_ε relation of notched specimens agreed with that of smooth specimens.
- 社団法人日本機械学会の論文
- 1989-01-25
著者
関連論文
- SFVV 3 鋼の疲労き裂進展下限界特性に及ぼす高温酸化被膜の効果
- 中・高温大気中におけるSFVV3 鋼の疲労き裂進展特性とき裂開閉口
- プログラム荷重下の疲労き裂進展とき裂開閉口の評価
- 超音波法による弾塑性破壊抵抗の評価に関する研究 : 第2報, 単調増加および繰返し荷重下の破壊抵抗曲線
- コンパクト試験片の疲労き裂開閉口挙動の解析的検討
- Rising Load法による応力腐食割れの下限界特性の評価
- SFVV 3 鋼の疲労き裂開閉口の実測と下限界特性の評価
- 超音波法による弾塑性破壊抵抗の評価に関する研究 : 第1報,提案する単一小形試験片による弾塑性破壊抵抗曲線の測定法
- アルミニウム合金5083-Oの安定破壊過程のフラクトグラフィ的検討
- A533B-1鋼の弾塑性破壊じん性および破壊抵抗の評価
- 超音波法による安定破壊開始点の検出と単一試験片による弾塑性破壊じん性の評価
- 超音波法によるSCM435鋼の疲労き裂進展特性の評価
- 疲労き裂から理想き裂への遷移について
- アルミニウム合金の疲労き裂進展抵抗
- 108 疲労き裂進展の遅れ遅延現象とき裂開閉口(疲労き裂)
- 107 アルミニウム合金の疲労き裂進展の下限界特性(疲労き裂)
- アルミニウム合金の安定破壊機構のフラクトグラフィ的検討
- 疲労き裂進展に及ぼす荷重変動効果のフラクトグラフィ的研究
- コンパクト試験片の破面粗さおよび酸化物誘起き裂閉口の有限要素解析
- 塑性 / 破面粗さおよび酸化物誘起き裂閉口の修正Dugdaleモデルによる解析
- 低サイクル疲労をうける切欠材でのき裂進展挙動
- 双曲線弓形断面軸のねじり
- スプライン状横断面の軸のねじり-1・2-