グラスセラミックスの破壊強度に及ぼす静水圧効果
スポンサーリンク
概要
- 論文の詳細を見る
In order to examine hydrostatic stress effects on the fracture strength of brittle material subjected to multiaxial stress states, glass ceramic specimens with an indentation-induced flaw were tested by four point bending under both atmospheric and hydrostatic pressures of up to about 100 MPa. The tests were conducted under both low and high stressing rates to provide data for different conditions of subcritical crack growth for the respective cases. The maximum tensile stress at fracture clearly increased with hydrostatic pressure in high stressing rate tests, though little significant difference was observed in strengths in low stressing rate tests. Such increase in fracture strength under high stressing rate conditions was attributed to the fact that the subcritical crack growth in region III which depend on the crack tip structure in the glass ceramics would be restricted by hydrostatic pressure ; because of this, a wide cohesive region at the crack tip favors abrupt fracture.
- 社団法人日本機械学会の論文
- 1991-10-25
著者
関連論文
- リサイクル設計を考慮した衝撃リベット締結法(機械要素,潤滑,設計,生産加工,生産システムなど)
- 衝撃リベット締結法による冷間圧延鋼板の接合
- ワッシャーを用いたリベット締結法の提案とその効果(機械要素,潤滑,工作,生産管理など)
- ワッシャーを用いた異種材のリベット締結
- Au薄膜を用いたき裂長さ測定法によるフロートガラスおよび熱強化ガラスのき裂進展特性評価
- 304 熱強化ガラスのき裂進展解析(OS 材料・構造の動的特性(1))
- ワッシャーを用いた異種材のリベット締結
- 廃棄ガラス繊維強化プラスチックを再利用した高強度多孔質タイルの開発
- 産業廃棄物を利用した高強度ガラスセラミックスの開発
- D34 アルミナのR曲線挙動 : コンプライアンス法によるき裂長さ測定法の評価(D3 材料力学(コンポジットレジン,セラミックス,木材の強度))