Effects of the Stress Amplitudes Below the Fatigue Limit on Fatigue Lives in the Cylindrical Specimens Having a V-shape Groove

スポンサーリンク

概要

• 論文の詳細を見る

• The effects of the stress amplitudes below the fatigue limit on the fatigue lives were investigated by the two steps multi-fold program fatigue tests in which the higher stress was above the fatigue limit and the lower stress was below the fatigue limit. Cylindrical specimens having V-shape groove of the structural carbon steel JIS S35C were used, and the stress concentration factors α of the specimens were selected as 2, 4 and 6. The test results revealed that the cumulative cycle ratios of the program fatigue tests were from 0.2 to 0.6 when α was 2, from 0.8 to 1.2 when α was 4, and from 0.9 to 1.4 when α was 6. The following behavior was also clarified : the fatigue crack was propagated even by the stress amplitude below the fatigue limit and in most cases the crack propagation was stopped as the number of cycles increased. Some discussions were made on the experimental results.

• 一般社団法人日本機械学会の論文

著者

• Kawada Yuichi

  Tokyo Metropolitan University

• Kawada Yuichi

  Tokyo Metropolitan College Of Engineering

• MISAWA Hiroshi

  Faculty of Technology, Tokyo Metroplitan Univ.

• Misawa Hiroshi

  Faculty Of Technology Tokyo Metropolitan University

• Misawa Hiroshi

  Faculty Of Engineering Tokyo Metropolitan University

関連論文

• Some Experiments on the Fatigue Life under Double and Triple Stresses
• On the Crack Propagation by Cyclic Stresses below the Fatigue Limit in Specimens with a Pinhole
• Fatigue Strength of Plain and Notched Bars under Pulsating Load Varying in Two Stages
• The Effect of Stress Amplitude below the Fatigue Limit on Cumulative Fatigue Lives in Perforated Round Specimens
• On Axially Symmetrical Residual Stresses in Bars with Longitudinally Nonuniform Stress Distribution
• Effects of the Stress Amplitudes Below the Fatigue Limit on Fatigue Lives in the Cylindrical Specimens Having a V-shape Groove
• The Crack Propagation by the Stress Amplitude below the Fatigue Limit
• A Study on the Residual Stress Distributions by Turning
• A ΔK_th Testing Method based on the Plastic Zone Slze at the Fatigue Crack Tip
• Fatigue Crack Propagation Behavior in 2024-T 3 Aluminium Alloys under Simplified Flight-Simulation Loading : Series A : Solid-Mechanics, Strength of Materials
• Effect of a Very Small Number of Stress Cycles above Fatigue Limit on Crack Propagation Behavior under Variable Stress Amplitude