Estimation of Corrosion Fatigue Lives Based on the Variations of the Crack Lengths Distributions During Stress Cycling
スポンサーリンク
概要
- 論文の詳細を見る
rights: 本文データは社団法人日本機械学会の許諾に基づきCiNiiから複製したものであるMany small distributed cracks have been observed on the specimen during corrosion fatigue process, and the damage of corrosion fatigue is related to the behaviour of these distributed cracks. The distribution of crack lengths during corrosion fatigue was approximated well by the three parameter Weibull distribution under plane-bending fatigue tests of carbon steel in salt water. A method of estimation of corrosion fatigue lives was proposed. The crack initiation, crack growth behaviour and the variation of the distribution of crack lengths during corrosion fatigue process were taken into consideration in the method. Comparing the estimated results with experimental results, it was concluded that this method could estimate the corrosion fatigue lives with good accuracy.
- 一般社団法人日本機械学会の論文
著者
-
MIYAO Kazyu
Faculty of Engineering, Toyama University
-
Miyao K
Faculty Of Engineering Toyama University
-
Miyao Kazyu
Faculty Of Engineering Toyama University
-
Ishihara S
Toyama Univ. Toyama City Jpn
-
Ishihara Sotomi
Faculty Of Engineering Toyama University
-
SHIOZAWA Kazuaki
Faculty of Engineering, Toyama University
-
MAEKAWA Ichiro
Faculty of Engineering, Tohoku University
-
Maekawa Ichiro
Faculty Of Engineering Tohoku University
-
Maekawa Ichiro
Faculty Of Engineering Niigata University
-
Shiozawa Kazuaki
Faculty Of Engineering Toyama University
関連論文
- 高速度工具鋼の超高サイクル疲労強度特性に及ぼす表面残留応力および介在物寸法の影響
- マグネシウム合金AZ80展伸材のギガサイクル疲労挙動とフラクトグラフィ
- 103 展伸マグネシウム合金AZ31の全ひずみ制御低サイクル疲労強度特性(OS1-1 マグネ合金・チタン合金の強度と評価,オーガナイズドセッション:1 先進材料の強度と評価)
- 102 展伸マグネシウム合金AZ31およびAZ61の超高サイクル疲労強度特性(OS1-1 マグネ合金・チタン合金の強度と評価,オーガナイズドセッション:1 先進材料の強度と評価)
- 634 マグネシウム合金AZ80押出し材の疲労強度に及ぼす時効処理の影響(非鉄金属,疲労破壊の防止と評価,オーガナイスドセッション1)
- 2302 Mg合金押出し材の低サイクル疲労強度特性に関する研究(S07-1 マグネシウム合金の疲労,S07 構造材料の疲労強度とき裂進展問題)
- OS0719 マグネシウム合金AZ31及びAZ61押出し材の超高サイクル疲労強度特性(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)
- OS0706 高速度工具鋼の超高サイクル疲労強度特性に及ぼす荷重負荷様式の影響(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)
- 2025 高炭素クロム軸受鋼Gcr15の超高サイクル疲労特性(S11-1 高強度鋼・高硬度鋼の超高サイクル疲労,S11 金属材料の超高サイクル疲労特性の解明)
- 2026 高速度工具鋼SKH51の高サイクルねじり疲労強度特性(S11-1 高強度鋼・高硬度鋼の超高サイクル疲労,S11 金属材料の超高サイクル疲労特性の解明)
- OS0707 開発マトリックスハイスの超高サイクル回転曲げ疲労強度特性評価(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)
- 619 高強度鋼の高サイクル疲労に及ぼす表面圧縮残留応力の影響(高サイクル疲労I,オーガナイズドセッション1.疲労の計測・解析・評価)
- 内部破壊機構に基づいて開発した高速度鋼の超高サイクル疲労強度特性
- 628 高速度工具鋼SKH51の超高サイクルねじり疲労強度特性(超高サイクル・強度予測,疲労破壊の防止と評価,オーガナイスドセッション1)
- 3319 超高サイクル疲労における破壊モードの遷移に及ぼす応力比の影響(S22 金属材料および実機の超高サイクル疲労,S22 金属材料および実機の超高サイクル疲労)
- 3318 多連式軸荷重疲労試験機によるSUJ2鋼の超高サイクル確率疲労特性(S22 金属材料および実機の超高サイクル疲労,S22 金属材料および実機の超高サイクル疲労)
- S0301-2-4 軸受鋼の回転曲げ疲労におけるコーキシング効果(疲労特性に及ぼす各種因子の影響(2))
- 112 高速度工具鋼の超高サイクル軸荷重疲労強度特性(OS1-3 鉄鋼・アルミ合金の強度と評価,オーガナイズドセッション:1 先進材料の強度と評価)
- 620 軸受鋼SUJ2の軸荷重疲労試験における内部き裂発生・進展に関するFRASTA解析(高サイクル疲労II,オーガナイズドセッション1.疲労の計測・解析・評価)
- 515 アルミニウム合金の回転曲げ疲労強度特性に及ぼすスパロール加工の影響(OS7(1) 表面改質による高機能化)
- Study on the Thermal Shock Behavior of Cermets and Cemented Carbides
- 高速度工具鋼SKH51の内部疲労破壊に及ぼす応力比の影響
- Computer Simulation of Corrosion Fatigue Process Considering Stress Relaxation Due to Initiation and Propagation of Multiple Cracks
- Growth of Crack in Steel by Impact Tension
- On the Anisotropy of the Fatigue Strength of Bearing Steel
- Effect of Flaws in Coating Film on Fatigue Strength of Steel Coated with Titanium Nitride
- Surface Crack Growth Path and Fatigue Life Prediction Due to Repeated Rolling/Sliding Contact
- Thermomechanical Effects due to Hot Rolling Contact on the Energy Release Rates of Multiple Interface Cracks in Layered Media
- Mutual Interference of Two Subsurface Cracks in a Semi-Infinite Body Due to Rolling Contact with Frictional Heating
- Distribution of Corrosion Fatigue Crack Lengths in Carbon Steel : 2nd Report, The Distributed Cracks which Interact and Coalesce
- Effects of Fluid Flow Rate and Stress Amplitude on the Initiation and Growth Behavior of Corrosion Pits on an Annealed Carbon Steel
- Estimation of Corrosion Fatigue Lives Based on the Variations of the Crack Lengths Distributions During Stress Cycling
- Distribution of Corrosion Fatigue Crack Lengths in Carbon Steel : 1st Report, The Cracks Which Grow Individually
- Stresses in a Circular Disk with an Eccentric Circular Hole Fixed at its Center and under a Tangential Force on the Outer Edge
- Stresses in a Plate Containing a Circular Hole with a Notch
- Crack Propagation behavior under Low-Cycle Corrosion Fatigue of A7003-T6 Aluminum Alloy
- OS1502 マグネシウム合金AZ61押出し材の疲労強度特性に及ぼす応力比の影響(金属材料の超高サイクル疲労と信頼性評価,オーガナイズドセッション)
- S0305-5-5 マグネシウム合金AZ80押出し材の疲労強度特性に及ぼす応力比の影響([S0305-5]超長寿命)
- S0305-5-3 ショットピーニング処理を施したマグネシウム合金AZ80押出し材の超高サイクル疲労特性([S0305-5]超長寿命)
- Study on the Interactioon of Fatigue Crack Propagation in Hybrid Bodies : Series A : Solid-Mechanics, Strength of Materials
- The Influence of Applied Stress Ratio on Fatigue Strength of TiN-coated Carbon Steel
- OS1512 高速度工具鋼YXR3の超高サイクル疲労強度特性に及ぼす表面残留応力の影響(OS15-03 種種の影響因子と解析・評価法,OS15 金属材料の超高サイクル疲労と信頼性評価)
- The Variation of the Notch Effect with the Variation of Notch Inclination Angle : Impact and Tension Experiment for the Rod Specimen with a V Groove
- OS0619 マグネシウム合金AZ80及びAZ61押出し材の低サイクル疲労挙動(OS06-05 材料強度の発現機構,OS06 微視構造を有する材料の変形と破壊(3))
- Thermal Stresses in a Plate Containing Two Circular Holes of Different Sizes under Uniform Heat Flow
- 1711 展伸マグネシウム合金の応力制御低サイクル疲労挙動に及ぼす変形異方性の影響(OS17-3 低サイクル疲労とその応用-規格化、多軸・異方性の検討-)
- 804 開発高速度工具鋼の超高サイクル疲労強度特性に及ぼす表面改質処理の影響(OS3-1 表面,皮膜材の強度評価,オーガナイズドセッション:3 表面・薄膜・接合部の力学特性と信頼性評価)
- 803 展伸マグネシウム合金AZ80の超高サイクル疲労挙動に及ぼすショットピーニング処理の影響(OS3-1 表面,皮膜材の強度評価,オーガナイズドセッション:3 表面・薄膜・接合部の力学特性と信頼性評価)
- 513 マトリックスハイスの超高サイクル回転曲げ疲労強度特性評価に関する研究(GS8-3 材料力学)
- 506 展伸マグネシウム合金AZ80の疲労強度特性に及ぼす応力比の影響(GS8-1 材料力学)
- 706 超高サイクル域における高強度鋼の疲労寿命推定法(高サイクル疲労特性,疲労損傷観察ならびに強度評価,オーガナイスドセッション1)
- 706 マグネシウム合金AZ31押出し材のひずみ制御低サイクル疲労挙動(マグネシウム合金の疲労I,疲労損傷の機構解明と評価,オーガナイスドセッション1)
- 708 展伸マグネシウム合金AZ80の超高サイクル域の疲労に及ぼす二段二重変動応力の影響(マグネシウム合金の疲労II,疲労損傷の機構解明と評価,オーガナイスドセッション1)
- 512 内部破壊機構に基づいて開発した高速度鋼の超高サイクル疲労強度特性(超高サイクル疲労II,疲労研究の課題と展望,オーガナイスドセッション1)
- 511 窒化処理を施した開発高速度工具鋼の超高サイクル疲労強度特性(超高サイクル疲労II,疲労研究の課題と展望,オーガナイスドセッション1)
- 510 疲労強度向上を狙った開発高速度工具鋼の超高サイクル疲労特性評価(超高サイクル疲労II,疲労研究の課題と展望,オーガナイスドセッション1)
- 707 マグネシウム合金AZ80押出し材の高サイクル軸荷重疲労強度特性に及ぼす応力比の影響(マグネシウム合金の疲労I,疲労損傷の機構解明と評価,オーガナイスドセッション1)
- Fatigue Crack Growth Behavior of Subsurface Crack in a Semi-Infinite Body Due to Rolling-Sliding Contact
- OS2018 マグネシウム合金押出し材の応力及びひずみ制御低サイクル疲労変形挙動と疲労寿命評価(OS20-4 疲労と強度,OS-20 HCP金属の実験力学と計算力学)
- OS0602 高強度鋼の超高サイクル域における疲労寿命の推定(OS6-1 基礎疲労特性と試験法・評価法,OS-6 金属材料の超高サイクル疲労と信頼性評価)