Studies on Press-Forming of Aluminum Alloys in the Coexisting State of Liquid and Solid : 2nd Report, Mechanical Properties of Extruded Aluminum Alloys.
スポンサーリンク
概要
- 論文の詳細を見る
In order to get the fundamental data about the extrusion method in the coexisting state of liquid and solid in Al-4Cu alloys with magnesium, the influences of extruding pressure, billet temperature and magnesium content on the mechanical properties of the extruded product have been investigated. The tensile strength of the extruded product fluctuates with the billet temperature. As the temperature falls, in other words, as the solid component increases, the tensile strength at first increases and after reaching a maximum, it begins to decrease and thereafter it begins to increase again. The microstructure of the extruded product consists of two different grains. One of them is the same which existed during extrusion and the other one is the grain that appears during cooling.
- 一般社団法人日本機械学会の論文
著者
-
ASAEDA Toshio
Tokyo Institute of Technology
-
Yoshikawa Masanori
Tokyo Institute Of Technology
-
OOTO Toshihiro
Tokyo Institute of Technology
関連論文
- On Die Casting of Cast Iron : Study on Die Casting of Ferrous Alloys, 3rd Report
- Measurement of Gas Pressure in Die Cavity : Study on Die Casting of Ferrous Alloy, 2nd Report
- The Temperature Measurement of Die : Study on Die Casting of Ferrous Alloys, 1st Report
- On the Superfinishing of the Convex Surface with Newly Developed MPR Stones
- Studies on Copper-Glass Compacts
- On the Trially Manufactured High Speed Teleprinter
- Studies on Press-Forming of Aluminum Alloys under Coexisting State of Liquid and Solid. : 1st Report, Mechanical Properties of Press-Formed Aluminum Alloys.
- Studies on Compacting of Spherical Cast Iron Powders.
- Studies on Press-Forming of Aluminum Alloys in the Coexisting State of Liquid and Solid : 2nd Report, Mechanical Properties of Extruded Aluminum Alloys.
- Studies on Press-forming of Aluminum Alloys in the Coexisting State of Liquid and Solid : 3rd Report, Mechanical Properties of Injection-formed Aluminum Alloys