Fatigue Strength Characteristics of High-Strength Steel
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify the fatigue strength characteristics of lowalloy steels tempered at low temperature (150-200℃) or carburized in generated gas, rotating bending fatigue tests were conducted in laboratory air and dry air. The influence of moisture in air was only observed for the carburized steel. The low- temperature-tempered steel revealed two knees on the S-N diagram, and no fatigue limit was found up to 10^9cycles (9 months). The carburized steel revealed three knees and the fatigue limit was found over lO^8 cycles. When the fatigue test of carburized steel was carried out in dry air or the surface structure anomalies were removed, the fatigue strengths were improved, but neither knees nor fatigue limits were found up to 10^9 cycles. The reasons for this were discovered from the results of fractography and the equations proposed by Murakami et al. for the prediction of the fatigue limit of steel with microdefects.
- 一般社団法人日本機械学会の論文
- 1990-07-15
著者
-
Asami Katsutoshi
Department Of Mechanical Engineering Musashi Institute Of Technology
-
Emura Hideki
Department Of Mechanical Engineering Musashi Institute Of Technology