ウエザリング法によるアルミナセメントの長期強度の推定 : アルミナセメントの研究(第5報)

スポンサーリンク

概要

• 論文の詳細を見る

• In spite of the great importance for the maintenance of the aluminous cement buildings there have been only a few papers concerning the changes of the mechanical properties extending long times. This paper deals with the possibilities of finding out the method of prediction of the mechanical strength of aged mortar as early as possible. The results of the studies on the changes of the structure of hydrated aluminous cement during aging showed that the decomposition of aluminum hydrate, which took an important part in the mechanical strength, was accelerated remarkably by the cycle of wetting and drying as well as by exposing to sunlight. It was considered that the change of the strength of hydrated aluminous cement during long age may be found rather in a short period by an accelerated test using weather-meter, a well known apparatus for testing the aging effect of organic products. A good many specimens of aluminous cement mortars were subjected to weather-meter test, under 40% relative humidity at 35℃. During the test extending about 100 days they were exposed alternatively to the attacks of arc light and water spray (8 min/hr, 1 atm nozzle) . Every 5 days the crushing strength were measured to compare with those of naturally aged mortar. It was confirmed that the curve of weather-meter test was quite similar in form to that of natural aging, giving, however, in the first 30 days the change as large as that occurred in 3 years of natural aging.; both curves showed no change of strength therafter. The statistical consideration of the experimental data indicated that 10 days of the artificial weathring corresponded to a year in natural aging. Thus, the change of the mechanical strength of hydrated aluminous cement may be predicted by using weather-meter test which gives the values of natural aging test 30 times or more earlier. [Received February 6,1962]

• 社団法人日本セラミックス協会の論文
• 1962-07-01

著者

• 小出 重明

  成蹊大学工学部工業化学科

• 小出 重明

  旭硝子株式会社研究所

関連論文

• 硬化アルミナ・セメント・モルタルの微構造に対する養生条件の影響
• 4成分Cao-Al_2O_3-Fe_2O_3-SiO_2系内化合物の水硬性に対するFe_2O_3およびSiO_2の影響
• 4成分CaO-Al_2O_3-Fe_2O_3-SiO_2の研究(系内化合物の示す水硬性の検討)
• プラズマフレームによる窒化物の合成
• プラズマフレームによる窒化物の合成
• Ca-Aluminateの初期水和に及ぼす添加剤の影響
• 単相電弧炉内の温度分布に関する理論的考察 : 高融点無機材料の研究 (第1報)
• β-Ca2Sioi4の結晶構造に関する添加剤の影響
• ウエザリング法によるアルミナセメントの長期強度の推定 : アルミナセメントの研究(第5報)
• アルミナセメントの水和反応

スポンサーリンク