ガラスバッチ溶融過程における少量添加剤の作用の高温顕微鏡による観察
スポンサーリンク
概要
- 論文の詳細を見る
After the pattern of Buss (Glas techn. Ber., 30,145 (1959)) a simple high temperature microscope was constructed, which, although with low magnification, was possible to follow after the glass melting process up to about 1450℃ by continuous observation. As the equipment has proved to be useful for present purpose a series of studies was made on the effect of the minor ingradients upon the melting process Na_2O-CaO-MgO-SiO_2 glass by observing the evolution of bubbles, change of the fluidity as well as the velocity of dissolution of quartz grains. The comparative test of 12 additional agents was carried out with a result showing that CaF_2,Li_2CO_3 and H_3BO_3 Were effective in the case of the maximum holding temperature of 1400℃.
- 社団法人日本セラミックス協会の論文
- 1963-01-01
著者
関連論文
- デビトライト(六ケイ酸三カルシウムニナトリウム)Ca_3Na_2Si_6O_の結晶構造
- びんガラス中のケイ酸質ガラスストーンの発生原因と生成機構
- ラマン分光法によるCaO-Al_2O_3-B_2O_3系ガラスの研究
- 溶融ガラス中でのケイ線石の挙動
- 溶融ガラス中での紅柱石の挙動
- アルミン酸八ホウ酸三カリウム、K_3AIB_8O_ の結晶構造
- CaO-Ga_2O_3-B_2O_3系ガラスのホウ素の配位数と物性(セラミック材料小特集)
- ラマン分光法によるCaO-Ga_2O_3-B_2O_3系ガラスの研究
- 紅柱石-絹雲母系の高温反応
- ガラス原料用ケイ砂の性質とガラスストーンの関係
- 三ホウ酸リチウム, Li_2O・3B_2O_3 の結晶構造
- ホウアルミン酸, 9Al_2O_3・2B_2O_3 の結晶構造
- ホウケイ酸カリウム, K_2O・B_2O_3・4SiO_2の結晶構造
- ホウケイ酸ストロンチウム, 4SrO・B_2O_3・SiO_2の結晶構造
- 気相反応によるLi2O-B2O3二成分化合物の合成
- 硼アルミン酸2ストロンチウム, 2SrO・Al_2O_3・B_2O_3の結晶構造
- Li_2O-B_2O_3-GeO_2系における準安定不混和域
- LiO_2O-B_2O_3-GeO_2系ガラスの物性と構造について
- ガラスなど非理想溶液の部分モル容積概念の検討と非理想溶液の理想溶液化
- 硼ゲルマン酸リチウム, Li_2O・B_2O_3・2GeO_2 の結晶構造
- バブリングの気泡の大きさに対する諸因子の作用の縮尺模型による推定
- 耐火性酸化物と熔融ガラス間の起電力について : 熔融ガラスの耐火物に対する侵蝕に関する電気化学的研究 (第1報)
- 鉄・マンガン着色ガラスの分光学的研究 : 着色ガラスの分光学的研究 第1報
- B2.ブラジル産燐酸アルミニウム鉱の鉱物学的研究(研究発表講演要旨)
- ガラスバッチ溶融過程における少量添加剤の作用の高温顕微鏡による観察
- 半透性隔壁を利用する珪酸塩濃淡電池系の起電力の測定