ジルコン煉瓦製造における (CrO_3+MgO) 水溶液添加の効果
スポンサーリンク
概要
- 論文の詳細を見る
Some concentrated (CrO3+MgO) aqua were added into zircon powder in order to improve corrosive resistance of zircon brick by both promoting the sintering of zircon and by strengthening the structure after firing at 1500°C and 1600°C in air or reduction atmosphere. Their effects on sintering and dissociation of zircon, and corrosive resistance of specimens after firing were investigated.The results were as follows.Concentrated (CrO3+MgO) aqua promoted sintering of zircon without dissociation in air atmosphere, and it promoted remarkably with slight dissociation in reduction atmosphere.And, it improved more the corrosive resistance of zircon brick, especially on slag penetration, than Cr2O3.
- 社団法人日本セラミックス協会の論文
- 1975-08-01
著者
関連論文
- 58 鋼中の非金属介在物の生成径路に関する研究(予報)(製銑および製鋼, 第 55 回講演大会講演大要)
- 95 製鋼スラグ中へのジルコンの溶解速度(耐火物・反応速度, 製鋼, 日本鉄鋼協会第 90 回(秋季)講演大会)
- 719 振動圧縮成形法によるアルミナセラミックスの作製(セラミックス, 萌芽・境界技術, 日本鉄鋼協会第 113 回(春季)講演大会)
- 溶銑予備処理用ソーダ系スラグによる耐火物の侵食(耐火物)(溶銑処理の発展)
- 147 Na_2CO_3-SiO_2 溶融物に対する耐火物の耐食性(耐火物・脱ガス, 製鋼, 日本鉄鋼協会第 103 回(秋季)講演大会)
- 熔触多成分系スラグ中へのジルコンの溶解速度
- 熔触2成分系スラグ中へのジルコン溶解速度
- 熔融酸化鉄中へのジルコンの溶解速度に影響をおよぼす2,3の因子について
- ジルコン煉瓦製造における (CrO_3+MgO) 水溶液添加の効果
- 熔融酸化鉄中へのアルミナの溶解速度
- 熔融 FeO 中へのジルコンの溶解速度
- ジルコン煉瓦の諸性質に及ぼすクロム化合物添加の影響
- 1500℃でのジルコンの焼結におよぼす酸化物の影響
- 85 ジルコンの解離, 解離ジルコンの再結合およびジルコンの合成速度(介在物, 製鋼, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
- 113 ジルコンの低温焼結におよぼす微量酸化物の影響(連続鋳造・造塊, 製鋼, 日本鉄鋼協会 第 78 回(秋季)講演大会)
- 34 ZrSiO_4-α・Al_2O_3 系及び ZrSiO_4-β・Al_2O_3 系焼結性の耐火物(製銑設備・耐火物その他, 製銑, 日本鉄鋼協会 第 76 回(秋季)講演大会)
- 84 酸化チタニウム含有ジルコン煉瓦の特性(造塊・応用・セミキルド・キルド・リムド介在物, 製銑・製鋼, 日本鉄鋼協会 第 74 回(秋季)講演大会)
- 130 塩基性耐火物の高温焼成による諸性貭の変化(製鋼, 日本鉄鋼協会第 72 回(秋季)講演大会講演)
- 39 塩基性平炉の天井に用いられた耐火物の X 線による研究(製鋼, 第 58 回講演大会講演大要)
- 塩基性平炉のゼブラ天井に用いられた耐火物の侵蝕機構に関する研究
- 14 ゼプラ天井における耐火物の侵蝕機構に関する研究(製鋼, 第 55 回講演大会講演大要)
- 平炉にしようされたクロマグ煉瓦のX線的研究 : 平炉にしようされた耐火物に関する研究 (第8報)
- 珪石煉瓦中のクリストバライトのX線的研究 : 平炉に使用された耐火物に関する研究 (第7報)