Li-Znフェライトの磁気的性質にV_2O_5添加の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effects of V2O5 addition on the magnetic properties of Li-Zn ferrites have been studied. Samples were fired at 1050-1150°C for 2 hours in air. The squareness ratio, sintered density, saturation magnetization, Curie temperature, and order-disorder transition of Li-Zn ferrites were determined as functions of V2O5 addition.The results obtained are summarized as follows.(1) The maximum squareness ratio (Br/Bm) were obtained by the addition of 0.1 wt% V2O5, but further increase in V2O5 content decreased Br/Bm.(2) The improvement of squareness ratio was due to the combination of small grain size and homogeneous grain size distribution.(3) It was found from saturation magnetization, Curie temperature and lattice constant that a portion of V2O5 dissolved into ferrite. The result support the B-site ordering which decreased with increasing V2O5 content. It was shown that the decrease in octahedral site ordering by the addition of V2O5 is attributed to the incorporation of V ions in the spinel lattice and also to the separation of α-Fe2O3.
- 社団法人日本セラミックス協会の論文
- 1976-09-01