ガラスより水中へ溶出するアルカリ・イオンの溶出量と溶出時間および溶出温度との関係式
スポンサーリンク
概要
- 論文の詳細を見る
Dissolving equation of alkali from glasses in silica-soda system was studied in this paper.Many kinds of glasses in system of (1) SiO2-Na2O-RO, (2) SiO2-Na2O-CaO, and SiO2-Na2O-ZnO, (3) SiO2-Na2O-(xRO+yR′O), (4) SiO2-Na2O-TiO2, and SiO2-Na2O-V2O5 were melted in electric furnace.The melted glasses were powdered into particles of 35-60 meshes and 2g of them were immersed in 50ml water of 30°, 40°, 50°, 60° and 70°C, while being stirred during 10, 20, 40, 80 and 160 minutes respectively.The results were as follows;1) The experimental data were tested by analysis of variance and it was found that log of dissolved amounts was linear function of log of dissolving time at constant dissolving temperature and the slopes of their linear equations were about 0.5.2) It was found that log of dissolved amounts was linear function of reciprocal of dissolving temperature at constant dissolving time and the slopes of their equations, that is, the apparent dissolution energy was approximately constant in all glasses.
- 社団法人日本セラミックス協会の論文
- 1972-11-01
著者
関連論文
- V_2O_5-P_2O_5系およびV_2O_5-P_2O_5-BaO系ガラスの化学的耐久性(続報)
- B_2O_3-V_2O_5-CaO系ガラスより水中へ溶出するバナジウムイオンおよびカルシウムイオンの挙動
- B_2O_3-V_2O_5-CaO系ガラスの化学的耐久性
- SiO_2-Na_2O系ガラス生成反応 : Na源としてNaOHを用いた場合
- B_2O_3-Fe_2O_3-R_2O (R : Na, K) 系ガラスの磁気的性質
- B_2O_3-TiO_2-BaO系ガラスより水中へ溶出するチタンイオンおよびバリウムイオンの挙動
- 遷移元素の酸化物を第3成分とするシリカ・ソーダ系ガラスの化学的耐久性(第2報) : SiO_2-Na_2O-TiO_2系
- 遷移元素の酸化物を第3成分とするシリカ・ソーダ系ガラスの化学的耐久性(第1報) : SiO_2-Na_2-V_2O_5系
- B_2O_3-SiO_2-Na_2O系ガラスの化学的耐久性
- P_2O_5-Na_2O系およびP_2O_5-Na_2O-Al_2O_3系ガラスの化学的耐久性
- 溶解度の異なる粉体から成る混合物(珪砂-炭酸ソーダ系)の溶解過程 : 粉体混合物の溶解現象に関する研究(第2報)
- ガラスより水中へ溶出する種々のイオンの溶出量と溶出時間および溶出温度との関係式
- ガラスより水中へ溶出するアルカリ・イオンの溶出量と溶出時間および溶出温度との関係式
- ガラス生成反応における数理統計的考察(第2報)
- ガラス生成反應における數理統計的考察 (第1報)