Ni基超合金単結晶の疲労強度に及ぼす応力波形の影響
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue strength of single crystal of a nickel-base superalloy(PWA1480)was studied. The stress-controlled fatigue tests were performed at 700°C and 5 Hz using triangular waveforms. In this study, two kinds of testing procedures were adopted. One is the conventional zero-tension fatigue test(R=0). Another is the procedure in which the maximum stress was held at 1000 MPa and the minimum stress was varied from zero to 1000 MPa(R=0〜1) at 24 and 700°C. The fatigue tests at higher mean stress levels caused creep-induced damage, which resulted in the inversion of the S-N curves at 700°C. The results of fatigue tests at 700°C indicated that the fracture mechanism changed depending on mean stress and also on stress range.
- 社団法人日本材料学会の論文
- 1998-03-15
著者
関連論文
- アルミ拡散コーティングを施した単結晶Ni基超合金のクリープ強度に及ぼす有害拡散層および熱処理の影響
- Inconel 718 の機械的特性に及ぼす熱処理の影響
- Ni基超合金単結晶CMSX-4のクリープ強度におよぼす2次析出γ'粒子の影響
- 102 Ni 基超合金単結晶 CMSX-4 の圧縮クリープ
- 101 Ni 基超合金単結晶 CMSX-4 の引張クリープ
- Ni基超合金単結晶CMSX-4のクリープ強度に及ぼす時効熱処理の影響
- Ni基超合金単結晶の高温強度に及ぼす{111}すべり系の活動の影響
- 簡便なデータベース作成法を用いた構造用鋼の熱処理シミュレーションの開発(加工・加工熱処理)
- 耐摩耗鋼板の機械的特性とミクロ組織に及ぼす軟化熱処理の影響(加工・加工熱処理)
- クリープの国際会議に参加して
- CMSX4のクリープ強度におよぼす時効熱処理の影響(高温強度)
- 単結晶Ni基超合金のクリープにおけるひずみ軟化
- 耐熱チタン合金DAT54の強度特性に及ぼす高温酸化の影響
- U720Liの引張/圧縮強度に及ぼす熱処理条件の影響
- 単結晶Ni基超合金の結晶塑性異方性と機械的特性 (特集 耐熱材料の開発の現状と展望)
- Influence of Primary and Secondary Crystallographic Orientations on Strengths of Nickel-based Superalloy Single Crystals
- クリーンラックによる単結晶Ni基超合金の疲労寿命と引張延性の低下
- 延性が最小となる温度でのCMSX2, CMSX4およびTMS-26のクリープ強度
- ピーク温度以上でのNi基超合金単結晶の高度強度に及ぼす結晶方位の影響
- Ni基超合金IN738LC単結晶の強度におよぼすγ′粒子の析出形態の影響
- Ni基超合金単結晶の高温強度に及ぼす塑性異方性の影響
- Ni基超合金単結晶の疲労強度に及ぼす結晶方位と応力波形の影響
- Ni基超合金単結晶の疲労強度に及ぼす応力波形の影響
- {111}すべり系に対する分解せん断応力一定で行った単結晶Ni基超合金のクリープ
- Inconel 718の微視組織と機械的特性に及ぼすTIG溶接の影響