模擬冷却水中でのさびこぶ発生要因
スポンサーリンク
概要
- 論文の詳細を見る
The factors causing tuberculation of carbon steels in a variety of synthetic cooling water have been investigated. A standard solution containing normal amounts of inorganic compounds was prepared as a synthetic cooling water, and it was concentrated several times to simulate practical operation of heat exchangers in the process industries. Tubercles formed on the steel tube covered with the mill scale, and the chemical composition of the water was a small factor in this case. The acid-pickled carbon steel tube experienced general corrosion in the standard solution, but was attacked seriously by the concentrated solutions to form tubercles. An important factor was found to be the corrosion potential, and it is necessary for the potential to remain at the transition region between active dissolution and passivation of carbon steel when tuberculation takes place.
- 社団法人日本材料学会の論文
- 1983-09-15
著者
関連論文
- 高濃縮模擬冷却水中におけるPO_4^(+Zn^)系防食剤による炭素鋼の孔食抑制効果(腐食防食小特集)
- 模擬冷却水中でのさびこぶ発生要因
- 伝熱を伴うステンレス鋼の食塩水溶液中における孔食挙動
- 炭素鋼のスラリーによる磨耗腐食(腐食防食小特集)
- 沸騰NaOH溶液中の鉄の伝熱腐食に関する電気化学的研究(腐食防食小特集)
- 電気化学操作の金属腐食への応用(腐食防食小特集)
- 乱流域における鉄円管の酸素拡散律速型腐食
- 共同研究「フェライト系ステンレス鋼の工業的利用と試験法の研究」 (腐食防食小特集)
- 食塩を含む稀い苛性ソーダ溶液中での鉄の孔食
- 苛性ソーダ溶液中での鉄,ニッケル,およびオーステナイト系ステンレス鋼の電気化学特性に及ぼすClO_3^-の影響
- 1.腐食工学の概要 : 腐食防止 : (建設材料特集号)
- 腐食防食部門委員会のあゆみ(4)
- 腐食教育と学協会の役割
- ホウ酸-ホウ酸ナトリウム緩衝溶液中における鉄さびこぶの発生機構
- フェライト系ステンレス鋼の硫酸中での電気化学的挙動
- 高温高濃度アルカリ溶液中での鉄の孔食
- Fe^ の溶存酸素による酸化反応
- 酸性水溶液中での鉄腐食反応に及ぼすFe^の効果
- 鉄鋼の水溶液腐食試験に関する二,三の試み
- 電極電位測定に用いるLuggin-Haber Capillary について
- 酸・アルカリ工業の現状(酸と塩基)
- 鉄筋コンクリート中の鉄筋の腐食に関する試験法 (腐食防食小特集)
- コバルト電析薄膜の陽極酸化と磁気特性
- 高温高濃度苛性ソーダ中でのステンレス鋼の電気化学的特性
- 弱アルカリ溶液中におけるコバルトアノード酸化反応に及ぼすアンモニアの効果
- MgSO4とNaHCO3を含む孔食抑制剤のアルミニウム合金に対する効果