焼入した鋼の残留応力測定における補正因子の検討
スポンサーリンク
概要
- 論文の詳細を見る
For the X-ray measurement of the residual stress of hardened steel, as a consequence of line broadening, Koistinen proposed the necessity of using the correction factors such as the Lorentz-polarization factor and the absorption factor. Examination of these correction factors was made, using the specimens freed from residual stress. Comparison between strain gage measurement and X-ray measurement of applied stresses was also made. Methods of making the stress free specimens of applied stresses was also made. Methods of making the stress free specimens were: (1) Hot bath quenching (to minimize transformation stress) (2)Thinning of a massive plate by chemical polishing (to relieve residual stress) (3)Magnetic separation of grinding chips of hardened steel. As a result of experiments for stress free state, raw data showed compressive strain, while the data corrected for background and LPA showed zero and somewhat tensile strain respectively. Under loading conditions, the strain measured by X-ray, regardless of correction factors, corresponded to the applied stress within the error of 10kg/mm^2. As a consequence, for measuring residual stress of hardened steel, it is enough to make merely the background correction, suing (1+ν)/E=5.47×10^<-5 >mm^2/kg.
- 1966-12-15
著者
関連論文
- 664 オースカッティングにおける球状化熱処理(溶接・被削性, 性質, 日本鉄鋼協会 第 100 回(秋季)講演大会)
- 502 オースカッティングにおけるセラミック工具の刃先温度の測定(工具鋼・鍛鋼・マルエージ鋼・被削性・介在物, 性質, 日本鉄鋼協会 第 99 回(春季)講演大会)
- 焼き入れした軸受鋼のX線残留応用測定持廻り実験
- 焼入した鋼の残留応力測定における補正因子の検討
- ころがり接触による残留応力の変化
- 軸受鋼摩耗表面の残留応力の挙動
- 658 オースカッティングにおける切りくず生成の周期性(油井管・被削性・条鋼・線材, 性質, 日本鉄鋼協会第 102 回(秋季)講演大会)
- 軸受用鋼のISO規格
- 研削における表面損傷のX線による研究