平織ガラス/エポキシ積層板の落錘衝撃損傷

概要

論文の詳細を見る
A damage process for perforation of a plain woven glass/epoxy composite laminate was studied,using an instrumented falling weight impact test.Changes in the damage were investigated at various levels of impact energy.The damage process was divided into three deffernt stages,accotding to main crack growth with fiber breakage perpendicular to fiber directions.In the first stage,surface cracks grew.Then,through-thickness cracks propagated in the second stage.In the last stage,petal bending fracture occurred.After examining cracks by fluorescent penetrant method,the main crack area was calculated approximately.In the first and second stages,a linear relation between the crack area and the absorbed impact energy was obtained.Making use of the relation,quantitative characterization of the impact damage process can be achieved.
社団法人日本材料学会の論文
1993-07-15