組合せ繰返し荷重下の切欠き材における分布微小き裂のモデル化に基づいた余寿命評価

概要

論文の詳細を見る
A procedure to evaluate residual life under cyclic combined loadings was established for a given initial state of distributed small cracks. Distributed cracks at the initial stage were modeled as straightline cracks by using an image-processing technique. The algorithm for the analysis of the crack growth after the initial stage was constructed by taking account of both modes of the propagation as a single crack and the coalescence between propagating cracks. Fatigue tests under combined axialtorsional loadings with constant and variable amplitudes were also conducted using cyclindrical specimens of pure copper with circumferential blunt notches. The fatigue life was correlated with the equivalent plastic strain range. When Compared for the same value of the parameter, the fatigue life became longer with increasing shear compoment in the stress state at the notch root, while nosignificant difference was observed between two loading modes of constant and variable stress amplitudes. The fatigue life defined by the formation of crack with a specific length was evaluated based on the proposed procedure. The predicted life almost coincided with the experimental date. Cracking morphology was also simulated by using the present model to show good correspondence with experimental observations.
社団法人日本材料学会の論文
1993-01-15