鉄系記憶材料の強度と記憶特性に及ぼす温度とひずみ速度の効果
スポンサーリンク
概要
- 論文の詳細を見る
With a prospect of wide technical applications, shape memory alloy steel developed recently is attracting large attention because of its excellent machinability and economical merit. In the present study, the strength and the shape memory effect of Fe-9Cr-5Ni-14Mn-6Si were clarified at temperatures from 208K to 423K and at strain rates from 10^-4X10^2/sec. The results obtained are summarized as follows. (1) Independent of strain rate, a shape recovery ratio of 85 to 98% was obtained at temperatures from 273 to 293K. (2) The stress increased linearly with the logarithm of strain rate up to about 3% strain level. (3) The stress rose with temperature in the range of 273K to 370K, while it decreased with temperature outside of this range.
- 1991-07-15
著者
関連論文
- 繊維結合型セラミックス基複合材の曲げ破壊強度
- ダブルノッチ試験片を用いた長繊維強化型セラミックス基複合材の静的及び衝撃せん断強度評価
- カーボン長繊維強化型窒化ケイ素の衝撃三点曲げ試験(衝撃)
- 多チャンネル高速ディジタル測定器を援用した繊維強化型セラミックス複合材の衝撃曲げ試験法
- 金属間化合物γ-TiAlの衝撃変形強度
- 衝撃荷重下におけるカーボン長繊維強化型窒化ケイ素の圧縮強度
- すべり摩擦開始時の動的挙動
- β-Ti合金の衝撃強度
- 鉄系記憶材料の強度と記憶特性に及ぼす温度とひずみ速度の効果
- ホプキソン棒法によるFRPの衝撃三点曲げ試験
- DYMAT88国際会議に参加して
- チタン合金の衝撃強度
- 216 亜鉛単結晶の錐面すべりの温度および歪速度依存性
- 亜鉛単結晶の変形強度の温度およびひずみ速度依存性
- 亜鉛多結晶の強度の温度およびひずみ速度依存性
- 亜鉛単結晶の変形強度の温度およびひずみ速度依存性
- 亜鉛多結晶の強度と温度およびひずみ速度依存性
- 亜鉛多結晶の熱的回復と応力-ひずみ関係
- 3-24 ディジタル波形解析装置を用いたホプキンソン棒法