熱間金型鋼 SKD62 の疲労き裂進展特性に及ぼす高温焼入れの影響
スポンサーリンク
概要
- 論文の詳細を見る
The fatigue crack growth behavior of hot work die steel SKD62, which was austenitized at 1025℃, 1100℃, and 1200℃ and subseuently quenched and tempered at 560℃〜650℃, was investigated. The fatigue test was carried out on a ΔK control sevohydraulic testmachine, by using compact -tension specimen. The impact test was carried out on an instrumented Charpy impact test machine. The results are summarized as follows. (1) For steels with high hardness (about H_v 600) after tempering at 560℃〜570℃, the fatigue fracture toughness K_<fc> was found to increase by raising the austenitizing temperature from 1025℃ to 1100℃. The increase of K_<fc> is presumably attributed to the decrease of undissolved carbides due to increased austenitizing temperature. However, there waas no further increase in K_<fc> for the increase of austenitizing temperature from 1100℃ to 1200℃. (2) For steels with low hardness (about H_v 400) after tempering at 640℃〜650℃, the K_<fc> was found to decrease with increasing austenitizing temperature. This may be attributed to the embrittlement of grain boundaries by raising both the austenitizing and the tempering temperatures. (3) At the linear region in the da/dN versus ΔK curve, the crack growth rate was not affected by the austenitizing temperature but decreased slightly with the rise of tempering temperature. The crack growth rate in this region could be correlated with the effective stress intensity factor range K_<eff>, regardless of tempering temperature. (4) The Charpy impact value decreased with the rise of asutenitizing temperature, regardless of tempering temperature. This trend did not agree with the K_<fc> mentioned above, because the Charpy impact value in this case mainly reflected the resistance to crack initiation.
- 社団法人日本材料学会の論文
- 1989-11-15
著者
関連論文
- 熱間金型鋼の熱間鍛造時に関する疲労亀裂進展
- 共晶はんだ63Snー37Pbの疲労寿命に及ぼす温度, 繰返し速度, ひずみ保持の影響
- ダイカスト用金型鋼の疲労亀裂進展特性
- はんだ接合部の弾性クリープ有限要素解析と拡散形半導体ゲージを用いた実験検証
- 電子部品はんだ接合部の熱疲労寿命解析
- 塑性締めボルトの疲労強度 : 再使用時の疲労強度保証
- 131 塑性締めボルトの疲労強度 : 再使用時の疲労強度保証(疲労強度II)
- 熱間金型材料の疲労亀裂進展特性
- 熱間金型鋼SKD62の疲労き裂進展特性に及ぼす焼入冷却速度の影響
- 熱間金型鋼 SKD62 の疲労き裂進展特性に及ぼす高温焼入れの影響
- 101 焼入冷却速度による熱間型鋼SKD62の疲労き裂進展特性の変化(疲労き裂進展)
- 109 熱間金型鋼SKD62の疲労き裂進展特性に及ぼす高温焼入れの影響(疲労き裂進展に対する影響因子)
- 鉄系焼結材料の切欠き疲労強度の破壊力学的解析
- 浸炭鋼のピッチング疲労強度に及ぼすショットピーニングの影響
- 浸炭鋼のピッチング疲労強度に及ぼす硬化層硬さの影響
- 浸炭鋼のピッチング疲労強度に及ぼす滑りの影響
- 浸炭鋼のピッチング強度解析と寿命予測
- 浸炭鋼のピッチング疲労強度に及ぼす浸炭異常層,表面粗さの影響
- ショットピーニングによる歯車の高強度化 : 歯形形状に対するショット粒径と投射角度の最適化
- 回転曲げ疲労を受けたVC被覆鋼の破壊点近傍の表面き裂について
- ショットピーニングによる残留応力の発生機構と疲労強度に及ぼす影響
- 浸炭焼入れ鋼の切欠曲げ疲労強度に及ぼす残留応力と平均応力の影響
- ショットピーニングにより浸炭焼入れ鋼に付与される残留応力の理論的予測と実験検証
- ショットピーニングと化学研磨による浸炭焼入れ鋼の疲労強度向上
- 空気噴射式ショットピーニングにおける粒子速度の測定と解析
- 塩水腐食した熱間圧延鋼板の疲労郷土低下要因の検討
- 常圧焼結窒化けい素の常温における曲げ疲労強度