細束X線による微小領域の応力測定に関する検討
スポンサーリンク
概要
- 論文の詳細を見る
A new type X-ray microbeam equipment which is capable of three-dimensional oscillation at an X-ray radiation position was used to measure the residual stress of pure iron powder and bending plate specimens as well as that in the vicinity of fatigue crack tip of 1/2 CT specimen. The results obtained are summerized as follows. (1) Diffraction profiles of pure iron powder with φ0.02〜0.03μm particle size obtained by the present microbeam technique in the beam area of 80μm in diameter and measuring time more than 800sec showed K_α1 and K_α2 peaks clearly, so that these profiles are good enough for stress measurement. (2) The measured stress of pure iron powder with φ10-25μm particle size in the beam area of 80μm in diameter was not equal to O MPa. The measured stress varied greatly and was independent of measuring time. (3) The measured stress of pure iron powder with φ0.02〜0.03μm particle size in the beam area of 80μm in diameter was almost 1 MPa, which shows the good accuracy of this X-ray micro-beam equipment. (4) The relation between the X-ray measured stress and the mechanically applied stress showed good agreement. (5) The distribution of residual stress at the vicinity of fatigue crack tip showed that the residual stress at the fatigue crack tip was compression and the residual stress in front of crack tip was tension. This tensile residual stress in front of crack tip existed in the area from 0.02 mm to 2 mm. (6) The above results show that the present equipment is advantageous in the investigation of 10cal stress, shortening the measuring time without sacrificing the accuracy.
- 社団法人日本材料学会の論文
- 1987-06-15
著者
関連論文
- 疲労過程における高分子材料の変形の微視的メカニズム
- 高分子材料の疲労強度に及ぼす温湿度効果の影響
- 高周波焼入材の疲労強度に及ぼす焼もどし温度の影響について
- 高周波焼入材の疲労強度向上に及ぼす要因について
- 高周波焼入材の疲労強度に及ぼす硬化深さ,および残留応力の影響
- 微小欠陥または介在物を含む高強度鋼の疲労強度に及ぼす平均応力の影響
- 切欠きを有する高周波焼入材の疲労強度向上に及ぼす要因について
- 1-28 切欠きを有する高周波焼入材の疲労強度に関する研究
- 疲労破面残留応力モデルの適用検討
- 高硬度材料の疲労破面残留応力モデルの検討
- 最大介在物寸法の推定法とそれに基づく高速度工具鋼の疲労限度の予測
- AEによる迅速耐久限度ばらつき評価技術の検討
- 疲労き裂開閉口挙動の残留応力的検討
- X線フラクトグラフィの冷間鍛造型への適用(X線材料強度小特集)
- フィッシュアイを伴う丸棒試験片のき裂進展挙動(X線材料強度小特集)
- 132 高速度工具鋼の疲労強度に関する研究(第5報) : 高硬度材の疲労破面残留応力モデルの検討(疲労強度)
- 細束X線による微小領域の応力測定に関する検討
- 301 細束X線による微小領域の応力測定に関する検討(応力測定・組織・複合材)
- 119 X 線による破面観察に関する研究 : 疲労破面の残留応力, 半価幅分布について
- 高周波焼入材の静曲げ強度および静的強度と疲労強度の関係
- 2-27 高周波焼入材の静曲げ強さおよび静的強さと耐久限の関係について
- 高周波焼入材の引張・圧縮疲労強度に及ぼす諸要因の影響
- 高速度工具鋼の引張・圧縮疲労破面のX線フラクトグラフィに関する検討(X線材料強度小特集)
- 高速度工具鋼の引張・圧縮疲労強度に及ぼす平均応力の影響に関する検討(X線材料強度小特集)
- 代替冷媒仕様カーエアコンとトライボロジー