高マンガンオーステナイト鋼のころがり疲労強度に及ぼす加工硬化の影響について

概要

論文の詳細を見る
The rolling contact fatigue tests were carried out on high manganese austenitic steel to investigate the influence of the work hardening phenomenon generated by repeated contact stress on the rolling contact fatigue strength by using a Nishihara-type wear testing machine under a lubricated state with a relative slip ratio of - 9%.The results obtained are summarized as follows : (1) In the cases that carbon contents were about 1.0 and 1.2%, high manganese austenitic steel had the same fatigue endurance limit (2 035 MPa), regardless of carbon content. (2) The rolling contact fatigue endurance limit of high manganese austenitic steel increased remarkably with work hardening generated by repeated contact stress. (3) The rolling contact fatigue endurance limit of high manganese austenitic steel increased remarkably compared with the austenitic stainless steel (SUS 304) having the same matrix structure as that of high manganese austenitic steel. (4) A crack of high manganese austenitic steel propagated along the boundary of the work hardening zone and the unwork hardening zone. The depth of crack propagation, at which the crack front became almost parallel to the contact surface, was fairly deeper than the maximum stress region calculated according to the maximum shearing stress theory.
社団法人日本材料学会の論文
1987-06-15