不飽和ポリエステル樹脂-炭酸カルシウム複合系の煮沸劣化に及ぼす炭酸カルシウムの配合効果

概要

論文の詳細を見る
The effect of incorporation of calcium carbonate (CaCO_3) on degradation of mechanical properties of a cured unsaturated polyester resin (UP)-CaCO_3 system in boiling water has been studied. The results showed that the incorporation of CaCO_3 increased remarkably the retention of flexural strength but decreased the retention of flexural modulus of the above system under the soaking condition in boiling water, while the incorporation of CaCO_3 decreased the initial flexural strength but increased remarkably the initial flexural modulus of the system. A mechanism of the degradation in boiling water was proposed that the decrease of flexural strength was mainly due to the degradation of UP component and that of flexural modulus was due to absorp-tion of water into the interface between UP and CaCO_3. Accordingly, the increase of CaCO_3 content which caused dilution of UP content increased the retention of flexural strength but decreased the retention of flexural modulus due to the increase of the interface between CaCO_3 and UP.
社団法人日本材料学会の論文
1977-07-15