片振り引張荷重下における鋳鉄の低サイクル疲労の一実験
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate the characteristic of the low cycle fatigue strength of gray cast iron, pulsating tension fatigue tests have been carried out by using notched and unnotched plate specimens of various sizes. The primary results obtained are summarized as follows: (1) The fatigue crack propagating rate dlc/dN is proportional to the n-th power of the stress intensity factor range ΔK regardless of the dimension of notch and the stress level. And the value of n is 7.5-9.1. (2) The apparent fracture toughness K_<IC> is hardly affected by the dimension of notch, but depends on the size of specimen. That is, K_<IC> of a large specimen is higher than those of smaller ones. (3) The notch factor β is about 1.1 in the case of the hole notch, and about 1.2-1.3 in the case of the key hole notch.
- 社団法人日本材料学会の論文
- 1974-09-15
著者
関連論文
- フェログラフィによるディ-ゼル主機潤滑油の分析
- 一定応力振幅下における圧入軸疲れ寿命のばらつき
- 二段多重重複荷重による大形圧入軸の曲げ疲れ試験
- 二段多重重複荷重による大形圧入軸の曲げ疲れ試験
- 腐食材の静的強度に関する実験的考察
- 腐食材の静的強度に関する実験的考察
- セラミックスの強度評価(第1報)
- プロペラ用鋳造材の疲労強度に関する統計的評価
- プロペラ用鋳造材の疲労強度に関する統計的評価
- 衝撃試験機の精度検査に対する統計的解析(技術一般)
- 鋳・鍛鋼品における2mmU及び5mmUノッチシャルピー吸収エネルギの関係について(技術一般)
- 独立型方形方式タンクタイプBの強度信頼性に関する実証的研究
- 独立型方形方式タンクタイプBの強度信頼性に関する実証的研究
- 推進軸系の損傷保守に及ぼす影響因子の数量的評価
- 船体損傷データの数量化理論による一解析
- 船体損傷データの数量化理論による一解析
- ピストン用アルミニウム合金の疲れ強さについて
- 大形鋳鍛鋼材の静的強度と疲労強度との対応について
- 折損クランク軸の曲げ疲れ強さの信頼性
- 主機系の損傷保全とその影響因子に関する統計的考察
- 推進軸系の損傷保守に及ぼす影響因子の数量的評価
- 片振り引張荷重下における鋳鉄の低サイクル疲労の一実験
- Lower Confidence Limit of Bending Fatigue Strength of Crankshaft Fractured in Service