チタンの疲労き裂進展に及ぼす応力繰返し速度の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effect of stress frequency on fatigue crack propagation in 99.5% pure titanium which has remarkable strain rate dependency in the plastic region was studied. Fatigue crack propagation tests were carried out under three kinds of stress frequencies (0.02, 0.2, 20 Hz). FEM elasto/visco-plastic analysis of fatigue crack propagation was performed, and the comparison between the dependency of crack propagation rate on stess frequency and the strain behavior at the crack tip calculated by the analysis was made. The results obtained in this study are summarized as follows: (1) It was found from the experiments that the crack propagation rate was approximately in inverse proportion to f^n(n>0), where f is the stress frequency. (2) The parameter closely related to the fatigue crack growth rate is the strain range Δε_y or visco-plastic strain range Δε_y^<vp> at the crack tip. (3) The effect of stress frequency on fatigue crack propagation rate may be explained by the variation of Δε_y or Δε_y^<vp> based on the strain rate dependency of material.
- 社団法人日本材料学会の論文
- 1982-11-15
著者
関連論文
- 非対称荷重を受ける厚肉軸対称かくの弾/粘塑性解析
- 疲労き裂伝ぱに及ぼす初期残留応力の影響
- 非対称荷重を受ける厚肉軸対称かくのクリープ変形問題
- チタンの疲労き裂進展に及ぼす応力繰返し速度の影響
- 厚肉回転対称かくの弾/粘塑性解析
- Limit Analysis of Spherical Shells under Internal Pressure
- 大ひずみ大変形を受ける薄肉円板の弾/粘塑性解析
- 230 爆接クラッド材のクリープき裂伝ぱ挙動
- 爆接クラッド材の疲労き裂伝ぱ
- 一般軸対称かくの弾/粘塑性変形
- 一般軸対称かくの弾/粘塑性変形
- 回転対称かくの大たわみ弾塑性クリープ問題
- 回転対称かくの大たわみ弾塑性クリープ問題
- 非対称荷重を受ける回転対称かくのクリープ変形
- 衝撃荷重を受ける一般軸対称かくの動的応答問題の一数値解法
- 粘弾性軸対称かくの非対称曲げ問題
- 一般軸対称かくの大たわみクリープ問題
- 二次元応力集中部の遷移クリープ解析
- 一般軸対称かくの遷移クリープ問題
- 一般軸対称かくの遷移クリープ問題 : 第1報, 数値解法
- 圧力容器の胴板突起部の強さに関する設計資料(続)
- 非対称荷重を受ける回転対称かくの弾/粘塑性解析
- スパイラル管の疲れ強さ
- スパイラル管の疲れ強さ
- 非対称荷重を受ける厚肉回転対称かくの弾/粘塑性動的応答
- 内圧を受ける圧力容器の銅板突起部の応力解析
- 内圧を受ける圧力容器の胴板突起部の応力解析
- 圧力容器の胴板突起部の疲れ強さ
- 引張りを受ける段付帯板の応力集中
- 引張りを受ける段付帯板の応力集中
- 疲労き裂発生に及ぼす繰返し速度の影響
- チタンの疲労き裂進展に及ぼす応力繰返し速度の変化の影響
- 薄肉かくの弾/粘塑性動的応答
- 回転対称かくの弾/粘塑性動的応答
- 圧力容器の胴板突起部の疲れ強さ