定電位電解法による銅ーニッケルークロムメッキの耐食性の評価
スポンサーリンク
概要
- 論文の詳細を見る
The evaluation by electrochemical study was made of the corrosion resistance of copper-nickel-chromium electroplates. Polarization curves were obtained in acid solution with or without chloride ion by the potentiostatic method. The metal specimens examined in the present study were as follows : (a) mild steel (b) copper plated from cyanide bath (c) sulfur containing bright nickel electroplate (d) sulfur-free semi-bright nickel electroplate (e) chromium plated from conventional bath (f) contact electrode in which two metal electrolyte (h) electroplated nickel-chromium plate. In general, bright nickels obtained from Watts type bath with sulfur containing addition agents such as 1,5-naphthalene disulfonate, saccharin, p-toluene and thiourea were found to be more active than sulfur-free semi-bright nickels. With increased sulfur content in the nickel deposits, the polarization curves were shifted to less noble potentials and the rate of corrosion of nickels increased remarkably inhibiting the passivation of nickel. It is found that chromium electrodeposits tend to become passive at less noble potentials than nickel in acid sulfate solution and the dissolution of chromium is very small compared with that of nickel at the potentials of -0.34~+0.10V vs. SCE. Corrosion of ni ckel-chromium electroplates at the potential region of the active state of nickel might correspond to the anodic dissolution of nickel through the pores or cracks in the chromium coating. By using the contact electrode and also coupling electrode systems in the measurement of polarization curves, it can be predicted that sulfur containing nickel plating on a sulfur-free semi-bright nickel will dissolve in preference to the semi-bright nickel exposed at coating defects and may result in the effective cathodic protection of the electroplated articles owing to the retardation of the rate of penetration into the double-layer nickel coatings. However, rapid corrosion penetration of the underlying nickel layer can be expected if the two layers do not have sufficiently different sulfur contents.
- 社団法人日本材料学会の論文
- 1968-08-15
著者
関連論文
- 合金アノ-ドを用いる光沢ニッケル-鉄合金めっき
- 蛍光顔料を用いるカラ-ニッケル分散めっき (分散めっき・合金めっき)
- 機能性金属めつき(電気めつき)(表面処理)
- 国際会議の紹介 : Interfinish(表面処理)
- クーロスタット法による無電解ニッケルめっき速度のモニタリング
- 複合めっきの現状と将来
- 分散めっき用粉体と分散めっき皮膜の性質 (「微粒子,分散系を利用した電気化学」特集号)
- Ni-Mn-S-SiC分散強化合金の電析 (〔電気化学協会〕創立50周年記念特集号) -- (コミュニケ-ション)
- 分散めっきの応用
- ジメチルホルムアルデヒド浴からのFe-Cr合金めっき
- Ni-Al2O3及びNi-ZrO2分散めっきの生成条件 (機能めっき)
- 定電位電解法による銅ーニッケルークロムメッキの耐食性の評価
- 無電解法によるNi-B-SiC複合皮膜の作製