金属組織の伸び変形の測定に基いた破断ひずみの推定
スポンサーリンク
概要
- 論文の詳細を見る
A quantitative metallographic study was performed on JIS SS400 steel to estimate the fracture strain from the measurement of aspect ratio for ferrite grains. The circumferentially notched round bar tensile specimens with the notch root radius of 6, 3, 1, 0.5 mm were employed to obtain a wide range of fracture strain. The relationship between plastic strain and aspect ratio for ferrite grains was obtained from the detailed metallographic observations on the polished and etched longitudinal midsection through the fractured half of smooth round bar tensile specimen. A large number of ferrite grains, plastically deformed to various strains, were examined carefully to determine the dependence of aspect ratio on plastic strain. The aspect ratio was well expressed by an exponential equation as a function of plastic strain. It was then possible to provide an appropriate estimate of the fracture strain of notched specimens from the above relation. The average aspect ratio of 9 views immediately underneath the fracture surface was used to deduce the fracture strain. The estimated values were found to be in reasonably good agreement with the measured values within an error of about 1 to 8 pct.
- 社団法人日本材料学会の論文
- 1996-04-15
著者
関連論文
- 切欠引張強さ比と限界ひずみ比の関係
- 切欠引張強さ比の応力三軸度およびひずみ硬化指数依存性
- フェライト結晶粒のアスペクト比の変化に基づいた破断ひずみの推定
- 腐食損傷を受けた構造部材の破壊挙動および強度劣化
- HW50鋼のディンプル破面率と破断ひずみとの関係
- 延性破断面の定量的評価に関する研究
- 鋼材の延性破断に及ぼす切欠鋭さ及び強度レベルの影響(資料)
- 球状黒鉛鋳鉄の破壊挙動およびマクロ破断面の変化特性
- 切欠の鈍い試験片における切欠引張強さ比とひずみ硬化指数の関係
- フェライト基地球状黒鉛鋳鉄のディンプル破断面の統計的評価
- ディンプルサイズの最大値分布と破壊挙動との関係
- 構造用鋼材におけるディンプル破断面の統計的評価
- 腐食部材の曲げ破壊挙動
- 103 構造用鋼材におけるディンプル破断面の定量的評価(腐食損傷・計測I)
- 317 球状黒鉛鋳鉄の破断面の定量的評価
- 球状黒鉛鋳鉄の引張破断面の定量的評価
- 417 球状黒鉛鋳鉄の破断ひずみと破断面粗さとの関係
- 金属組織の伸び変形の測定に基いた破断ひずみの推定
- 215 金属組織の微視的伸び変形の測定による破断ひずみの推定
- 025 シャルピー吸収エネルギーと破断ひずみの関係(GS4-1 一般セッション)