ZnO-PbOセラミックスの焼結挙動と電気的性質
スポンサーリンク
概要
- 論文の詳細を見る
ZnO doped with PbO in the range of 0.5 to 5 mol% was sintered at temperatures of 1273 to 1573 K, and microstructure and current-voltage characteristics were examined. Liquid Pb-rich Pb-Zn-O phase was penetrated among ZnO grains during sintering of ZnO-PbO composites, forming a grainboundary layer. However, PbO addition prevented densification during sintering due to the high vapor pressure of liquid PbO. The current-voltage behavior of the ZnO-PbO composites was non-linear. The resistivity of the ZnO-PbO composites decreased with increasing sintering temperature and approached that of pure ZnO. The non-linear coefficient of the ZnO-PbO composites is small, and hardly depends on the PbO content and the sintering temperature.
- 社団法人日本セラミックス協会の論文
- 2002-09-01
著者
関連論文
- 通電加圧焼結によるWC-W_2C-TiCセラミックスの合成とその機械的性質
- Nb_2O_5, TiO_2を添加したZnOバリスタの電気的性質
- 反応性通電加圧焼結によるWC-W2C複合セラミックスの合成とその機械的性質
- 放電プラズマ焼結法とは? : (1)材料創成への放電プラズマ焼結の適用
- B_4CとTiの反応性放電プラズマ焼結によるTi-B-C系複合体の合成
- 反応性放電プラズマ焼結によるTiB_2-Ti(CN)複合体の合成
- BNとTiの反応性放電プラズマ焼結によるTiB_2-TiN複合体の合成
- B_4CとTiの反応性放電プラズマ焼結法によるTiB_2-TiC複合体の合成
- 大正時代の秋田鉱山専門学校治金学科の実習報告書と卒業論文
- ZnO-PbOセラミックスの焼結挙動と電気的性質
- B_4CとTi粉体間の固相反応によるTiB_2-TiC複合体の合成