湿式合成されたPLZT粉末成形体中からの超臨界二酸化炭素によるステアリルアルコールの脱脂 : 合成・キャラクタリーゼーション
スポンサーリンク
概要
- 論文の詳細を見る
Different agglomerated powders of PLZT were prepared from aqueous nitrate solutions using two preparation methods. The microstructure developed during calcination at 450°-470℃ was determined by powder characteristics such as crystalline phase, particle morphology and size, agglomeration, and surface area. Green compacts containing 5 wt% stearyl alcohol binder were fabricated by uniaxial pressing. Extraction of the binder was carried out with supercritical carbon dioxide at 35°-65℃ under the pressure of 9.81 MPa or 19.6 MPa. The degree of agglomeration of calcined powders influenced the extraction. The extraction process is discussed on the basis of mass- transfer resistance in compacts and chemical affinity between powder surface and stearyl alcohol.
- 社団法人日本セラミックス協会の論文
- 1990-08-01
著者
関連論文
- 柔らかさおよび粘弾性を計測できる機能性試験機の開発(機械力学,計測,自動制御)
- W添加9-12%Crフェライト系耐熱鋼におけるクリープき裂成長寿命予測式の高精度化に及ぼす化学成分, 材料組織の影響
- 高温疲労・クリープ重畳条件下のき裂成長特性および損傷評価
- ポリエチレンのクリープ破壊特性 : 屋外暴露による劣化の影響
- スクラッチ試験による溶射被膜のインプロセス計測 - アルミナ被膜と自溶性合金被膜の AE 特性 -
- プラスチックフィルムの強度
- プラスチック材料のクリープき裂成長特性
- 微小押し込みき裂を有するガラスの破壊特性について
- 湿式合成されたPLZT粉末成形体中からの超臨界二酸化炭素によるステアリルアルコールの脱脂 : 合成・キャラクタリーゼーション
- CT試験片と押し込み誘起微小き製を含む曲げ試験片で評価したソーダ石灰ガラスのき裂成長特性 : 残留応力の影響
- 223 PMMA の疲労破壊について
- 柔らかさおよび粘弾性を計測できる機能性試験機の開発
- 202 フィルム状高分子材料の時間依存型破壊特性